Phase Precipitation Behavior of La2Fe14B and Ce2Fe14B Alloys During Melt Spinning and Heat Treatment:a Comparative Study

Zhenyang ZHANG,Lizhong ZHAO,Jiasheng ZHANG,Xichun ZHONG,Zhongwu LIU
DOI: https://doi.org/10.11896/j.issn.1005-023X.2018.08.013
2018-01-01
Abstract:To understand the structure,phase precipitation behavior and magnetic properties of ternary La2Fe14B and Ce2Fe14B alloys,the effects of wheel speed (10—50 m/s)of melt spinning and heat treatment on these alloys were investigated.The results show that,as for pun alloys,the hard magnetic 2:14:1 phase could not be obtained in La2Fe14B alloys,but it could be formed in Ce2Fe14B alloys.The phases ofα-Fe and La mainly precipitated in La2Fe14B ribbons at 10 m/s.However,the hard magnetic 2:14:1 phase precipitated in Ce2Fe14B ribbons at 10 m/s and 20 m/s.With the increase of wheel speed,the content of amorphous phase in-creased.For annealed La2Fe14B alloys,the results showed that α-Fe and La phases mainly precipitated from the amorphous matrix, and liquid La-rich regions andα-Fe phases could coexist.However,in the annealed Ce2Fe14B alloys,α-Fe phase precipitated first fol-lowed by the appearance of 2:14:1 phase and grain growth.In addition,the amorphous La2Fe14B alloy had higher cure temperature than Ce2Fe14B alloy,and it started to precipitateα-Fe phase at lower temperature.As a result,relatively good hard magnetic proper-ties with a certain coercivity could be obtained in Ce2Fe14B alloys due to the precipitation of hard magnetic 2:14:1 phase.This work will be valuable for exploring the La or Ce based rare earth permanent magnets.
What problem does this paper attempt to address?