Abstract:Silicon carbide (SiC) devices have the potential to yield new components with functional capabilities that far exceed components based on silicon devices. Selective doping of SiC by ion implantation is an important fabrication technology that must be completely understood if SiC devices are to achieve their potential. One major problem with ion implantation into SiC is the surface roughening that results from annealing SiC at the high temperatures which are needed to activate implanted acceptor ions, boron or aluminum. This paper examines the causes and possible solutions to surface roughening of implanted and annealed 4H-SiC. Samples consisting of n-type epilayers (5 × 1015 cm−3, 4 µm thick) on 4H-SiC substrates were implanted with B or Al to a total dose of 4 × 1014 cm−2 or 2 × 1015 cm−2, respectively. Roughness measurements were made using atomic force microscopy. From the variation of root mean square (rms) roughness with annealing temperature, apparent activation energies for roughening following implantation with Al and B were 1.1 and 2.2 eV, respectively, when annealed in argon. Time-dependent activation and surface morphology analyses show a sublinear dependence of implant activation on time; activation percentages after a 5 min anneal following boron implantation are about a factor of two less than after a 40 min anneal. The rms surface roughness remained relatively constant with time for anneals in argon at 1750°C. Roughness values at this temperature were approximately 8.0 nm. Annealing experiments performed in different ambients demonstrated the benefits of using silane to maintain good surface morphology. Roughnesses were 1.0 nm (rms) when boron or aluminum implants were annealed in silane at 1700°C, but were about 8 and 11 nm for B and Al, respectively, when annealed in argon at the same temperature.

Mechanical properties and indentation-induced phase transformation in 4H–SiC implanted by hydrogen ions

Nano-cutting mechanism of ion implantation-modified SiC: reducing subsurface damage expansion and abrasive wear

Improvement mechanism of brittle-plastic transition and residual stress in scratching 4H-SiC implanted by hydrogen ions

Molecular Dynamics Simulation of Ion-Implanted Single-Crystal 3C-Sic Nano-Indentation

Modification Mechanism of Collaborative Ions Implanted into 4H-Sic by Atomic Simulation and Experiment

Nanoindentation Study of Silicon-implanted Monocrystal Cubic Silicon Carbide

Atomistic Analysis on Implantation Effects of Hydrogen Ions and Copper Ions into 4H-Sic

Nano material removal mechanism of 4H-SiC in ion implantation-assisted machining

Molecular Dynamics of Nanometric Processing of Ion Implanted Monocrystalline Silicon Surfaces

Molecular dynamics analysis of the influence of ion implantation parameters on ultra-precision machining of silicon carbide

Surface and Interface Properties of Ion Implanted 4H-Silicon Carbide

Molecular dynamics simulation of silicon vacancy defects in silicon carbide by hydrogen ion implantation and subsequent annealing

Anisotropic Deformation of 4H-Sic Wafers: Insights from Nanoindentation Tests

Mechanical and tribological properties of single crystalline silicon implanted by C ions using MEVVA source

Influence of the C+-implantation on the Micro-Tribological Behavior of Silicon Wafer

Effect of Ion Irradiation on Nanoindentation Fracture and Deformation in Silicon Carbide

Molecular Dynamics Simulation of Ultra-Precision Machining 3C-Sic Assisted by Ion Implantation

Research on Nano-Mechanical and Micro-Tribological Behaviors of C+- Implanted Silicon

Surface roughening in ion implanted 4H-silicon carbide

Study on Mechanical Properties of Single-Crystal Silicon Carbide by Nanoindentation

Nanometric Cutting of Single Crystal Silicon Surfaces Modified by Ion Implantation