Failure Modes of Carbon Nanotubes in Cement Composites under Flexural Load

Xiaoran Wang,Qinghua Li,Shilang Xu

DOI: https://doi.org/10.1016/j.engfracmech.2022.108740

IF: 5.4

2022-01-01

Engineering Fracture Mechanics

Abstract:The carbon nanotube (CNT) reinforced cement composites have been attracting increasing interests, while there lacks experimental research on the influence of CNT failure modes on mechanical properties, especially for large content CNTs. In this study, the influence of CNT content on their failure modes is analyzed theoretically and the effect of CNT failure modes on the flexural properties of cement composites is investigated experimentally. It is found that further increasing the CNT content beyond the percolation threshold leads to the increase of flexural strength again (increased by 45.6%), even exceeding the strength at the percolation threshold (increased by 35.6%). Breaking and pulling-out failure modes are observed by SEM in the 0.5 vol% group and 1.5 vol% group, respectively. When the CNT content reaches the "critical content " (1.0 vol%), both the breaking and pulling-out failure modes exist but are not dominant, and the load-displacement curve exhibits a bimodal hump shape. The critical CNT content prevents composites from sudden failure but is in a stage of "pre-failure - re-strengthening - final-failure ". After the critical content, when the CNT content gets so large that the pulling-out failure mode is dominant, the flexural strength increases again.