Interstitial Migration Behavior and Defect Evolution in Ion Irradiated Pure Nickel and Ni-xFe Binary Alloys
Chenyang Lu,Taini Yang,Liangliang Niu,Qing Peng,Ke Jin,Miguel L. Crespillo,Gihan Velisa,Haizhou Xue,Feifei Zhang,Pengyuan Xiu,Yanwen Zhang,Fei Gao,Hongbin Bei,William J. Weber,Lumin Wang
DOI: https://doi.org/10.1016/j.jnucmat.2018.07.006
IF: 3.555
2018-01-01
Journal of Nuclear Materials
Abstract:Transition from long-range one-dimensional to short-range three-dimensional migration modes of interstitial defect clusters greatly reduces the damage accumulation in single-phase concentrated solid solution alloys under ion irradiation. A synergetic investigation with experimental, computational and modeling approaches revealed that both the resistance to void swelling and the delay in dislocation evolution in Ni-Fe alloys increased with iron concentration. This was attributed to the gradually increased sluggishness of defect migration, which enhances interstitial and vacancy recombination. Transition from long-range one-dimensional defect motion in pure nickel to short-range three-dimensional motion in concentrated Ni-Fe alloys is continuum, not abrupt, and within an iron concentration range up to 20%. The gradual transition process can be quantitatively characterized by the mean free path of the interstitial defect clusters.