Heating Effects on Fine Structure of a Cu-Al-Ni-Mn-Ti Shape Memory Alloy
WH ZOU,HY PENG,R WANG,J GUI,DZ YANG
DOI: https://doi.org/10.1016/0956-7151(95)00016-o
1995-01-01
Acta Metallurgica et Materialia
Abstract:The heating effects on the structure and fine structure of Cu-11.9Al-5Ni-1.6Mn-1Ti (wt%) shape memory alloy have been studied by means of transmission electron microscopy and microscopic compositional analysis. With the increase of the heating temperature and time, the stabilized M18R1 martensite, transformed from the parent phase of L21 structure type, underwent the following structural variations: M18R1 → N18R1 → disorder N9R. Disorder N9R bainite precipitates and retained parent phases were observed in specimens heated at 573 and 623 K for 7.2 kr or longer. When the alloy was heated at 673 K for 133.2 ks, equilibrium α, γ2 and Ni,Al-rich phases were formed without any retained β1 parent phase. While the size of the Xs particles decreased in the specimen heated at 623 K for 7.2 ks and they disappeared completely in the specimen heated at 673 K, the XL particles were coarsened after heating. With the increase of the heating temperature and time the growth of the antiphase domains was observed.