Space‐confined thermal disintegration synthesis of graphene‐copper nanohybrids for enhanced tribological behaviors of epoxy‐based composites

Yong Li,Junya Yuan,Guorong He,Liangfei Wu,Yanling Wang,Meng Liu,Xuehu Men
DOI: https://doi.org/10.1002/pc.25990
IF: 5.2
2021-02-20
Polymer Composites
Abstract:<p>Epoxy resin (EP) has received extensive attention in the field of mechanical engineering due to its outstanding physical mechanical performance and chemical stability. However, relatively weak thermal and abrasion properties seriously limit its application in motion conditions. Here, we report copper‐graphene nanohybrids (Cu‐G) prepared by a space‐confined thermal disintegration method as promising materials for improving the thermal and tribological properties of epoxy composites. Impressively, the thermal conductivity and stability properties of EP/Cu‐G composites present obvious enhancements compared to pure EP. Meanwhile, the tensile strength and elongation at break of EP/Cu‐G are increased by 8.0% and 7.5% compared to those of pure EP. In addition, sliding test results reveal that the wear rate of EP/Cu‐G composites show a 66.7% decline, which can be ascribed to the synergistic enhancement effects between graphene and Cu.</p>
materials science, composites,polymer science
What problem does this paper attempt to address?
This paper attempts to address the limitations of epoxy resin (EP) in mechanical engineering applications due to its weak thermal performance and wear resistance. Specifically, the authors synthesized copper-graphene nanohybrid material (Cu-G) via a confined space pyrolysis method and incorporated it as a reinforcement into the epoxy resin matrix to improve the thermal conductivity, stability, and wear resistance of the composite material. ### Main Issues Addressed by the Paper: 1. **Improving the thermal conductivity of epoxy resin**: The thermal conductivity of pure epoxy resin is relatively low, which limits its application under high-temperature conditions. By incorporating Cu-G nanohybrid material, the thermal conductivity of the epoxy resin composite can be significantly improved. 2. **Enhancing the wear resistance of epoxy resin**: Epoxy resin is prone to wear during friction, leading to a shortened service life. The addition of Cu-G nanohybrid material can significantly reduce the wear rate of the composite material, thereby enhancing its wear resistance. 3. **Improving the mechanical properties of epoxy resin**: Pure epoxy resin has high brittleness and is prone to crack propagation. The addition of Cu-G nanohybrid material can increase the tensile strength and elongation at break of the composite material, thereby improving its mechanical properties. ### Experimental Methods and Results: - **Material Preparation**: Cu-G nanohybrid material was synthesized via a confined space pyrolysis method and incorporated into the epoxy resin matrix to prepare EP/Cu-G composites. - **Performance Testing**: The performance of EP/Cu-G composites was systematically evaluated through thermal conductivity tests, thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), mechanical property tests, and friction and wear tests. - **Results Analysis**: - **Thermal Conductivity**: The thermal conductivity of EP/Cu-G composites increased with the Cu-G content, then slightly decreased. When the Cu-G content was 0.5 wt%, the thermal conductivity reached a maximum of 0.344 W/mK, an increase of 81.0% compared to pure epoxy resin. - **Thermal Stability**: The initial decomposition temperature and residual amount of EP/Cu-G composites increased, indicating that the addition of Cu-G improved the thermal stability of the composite material. - **Mechanical Properties**: The tensile strength and elongation at break of EP/Cu-G composites increased by 8.0% and 7.5%, respectively, indicating that the addition of Cu-G improved the mechanical properties of the composite material. - **Friction and Wear Performance**: The friction coefficient and wear rate of EP/Cu-G composites significantly decreased, especially when the Cu-G content was 0.5 wt%, the wear rate decreased by 66.7%. ### Conclusion: Incorporating Cu-G nanohybrid material into the epoxy resin matrix can significantly improve the thermal conductivity, thermal stability, and wear resistance of the composite material, while also enhancing its mechanical properties. These improvements make EP/Cu-G composites more promising for applications in the field of mechanical engineering.