Abstract:Advanced ceramics find significant application areas due to their superior mechanical, electrical, magnetic chemical and thermal properties. By combining these materials, significant properties can be obtained as a result of production of the composites of hard metal compounds in nanoscale dimensions. Self-propagated high-temperature synthesis (SHS) is one of the prominent methods for the production of such nanoparticles. SHS is a combustion synthesis method. In this study, nanocomposite powders of B4C-TiB2 were synthesized by SHS method. FactSage software was used for thermochemical simulation and computational stoichiometric optimization. In the experimental step, 2 different SHS sets were prepared. In the first stage, B4C and TiB2 powders were synthesized. The B4C-TiB2 composite was produced in the final set of experiments. Then, production parameters of B4C-TiB2 composite powders, from B2O3, TiO2, and carbon black, were investigated. Magnesium powder was used as reductant agent. Afterwards, HCl leaching process was performed, and acid concentration was optimized. The effect of carbonic acid and H2O2 addition on dissolution of undesired phases was also been investigated as a new method. Products were characterized by XRD, SEM and BET analysis. B4C-TiB2 composite powder with quite high surface area, fine particle size and high porosity could be synthesized with reasonable purity. According to the results, the optimum molar ratios were determined as TiO2:B2O3:Mg:C = 1:3:12:1.6. Optimum acid concentration was found to be 10.5 M for leaching process, and carbonic acid addition on leaching step found to be effective on TiO2 removal. The highest purity could be obtained with 50%-50% stoichiometry. It has also been determined that the synthesis of B4C-TiB2 composite powder has a positive effect on both the chemical content and the morphology that will increase the sintering ability.

Powder Synthesis, Densification, Microstructure and Mechanical Properties of Hfb2-Hfc Ceramic Composites

The Structure and Properties of the Promising Ultra-High-Temperature HfB2–HfC–SiC Ceramics Obtained from Heterophase SHS Powders

Enhancement mechanical properties of in-situ preparated B4C-based composites with small amount of (Ti3SiC2+Si)

Strengthening Hf0.95Ta0.05B2 Ceramic With Ultrafine Grains and High-density Dislocations

Pressureless densification of HfB2-based ceramics using HfB2 powders by borothermal reduction

B4C‒TiB2 composite with modified microstructure and enhanced properties from optimal size coupling of raw powders

Synergistic hardening in a dual phase high‐entropy (Hf,Nb,Ta,Ti,Zr)C–(Hf,Nb,Ta,Ti,Zr)B2 ultra‐high temperature ceramic

Influence of Y2O3 contents on sintering and mechanical properties of B4C-Al2O3 multiphase ceramic composites

Effects of Boron Content on the Microstructure and Properties of BxC-TiB2 (x=4.5, 6.5 or 8.5) Ceramic Composites by the Reactive Spark Plasma Sintering

Powder synthesis, densification, microstructure and mechanical properties of Hf-based ternary boride ceramics

Effect of synthetic Mo2FeB2 powder on the microstructure and mechanical properties of Mo2FeB2-based cermets

Ultra-fast high-temperature synthesis and densification of high-entropy diborides and diboride-carbide ceramics

Novel Synthesis of (Hf0.25zr0.25ti0.25ta0.25)c-Sic Biphasic Ceramic Micro-Powders Using Single-Source-precursor Route

Exceptional hardness and thermal properties of SiC/(Hf,Ta)C(N)/ (B)C ceramic composites derived from single‐source precursor

Production of B4C-TiB2 composite powder by self-propagating high-temperature synthesis

Low temperature sintering of Hf0.95Nb0.05B2-based ceramics with submicron-scaled grains and enhanced mechanical properties

Microstructure and mechanical properties of B4C based ceramics with Fe3Al as sintering aid by spark plasma sintering

Preparation and Sinterability of Submicron Titanium Carbide Powders Synthesized with Phenolic Resin As Carbon Source by Carbothermal Reduction

Synthesis and Characterization of High-Purity, High-Entropy Diboride Ceramic Powders by a Liquid Phase Method

Phase evolution and oxidation resistance of Si3N4/HfB2/HfB C N1–– ceramic nanocomposites prepared from tailored preceramic polymers

Microstructures and mechanical properties of high-entropy (Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C ceramics with the addition of SiC secondary phase