Robust Resistance Switching Performance in a Ca3Ti2O7/La0.67Sr0.33MnO3 Heterostructure Induced by the Interface
Jin Peng Cao,Wen Hao Tu,Xiang Fei Li,Wei Ye Deng,Zong Lin Lv,Hong Wei Wang,Jun Kun Wu,Tian Xiang Liu,Li Hong Yang,Xiao Qin Yan,Xin Chen,Qiang Li,Kun Lin,Jun Miao
DOI: https://doi.org/10.1063/5.0224630
IF: 4
2024-01-01
Applied Physics Letters
Abstract:Ruddlesden–Popper phase oxides, such as Ca3Ti2O7, have been established as hybrid improper ferroelectrics. However, investigations into Ca3Ti2O7 have primarily concentrated on their structural and ferroelectric properties. In this study, we prepared epitaxial Ca3Ti2O7 thin films via magnetron sputtering. Conducting atomic force microscopy was employed to characterize local current variations under an applied bias voltage. Electron paramagnetic resonance measurements of the Ca3Ti2O7/La0.67Sr0.33MnO3 film were conducted to assess its defect characteristics. Interestingly, the Ca3Ti2O7/La0.67Sr0.33MnO3 stacks exhibited remarkable macroscopic resistance switching, with a resistance on/off ratio reaching 100, alongside robust retention (∼2500 s) and endurance (∼2000 cycles) features. Additionally, density functional theory calculations suggest that the resistance switching is attributable to the interface barrier of the Ca3Ti2O7/La0.67Sr0.33MnO3 interface and the efficacy of space charge limitation. This work proposes an avenue for the utilization of Ruddlesden–Popper phase Ca3Ti2O7 in various applications.