Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Cyclic Deformation Response of Austenitic Ni-based Alloy: Mechanical Behavior, Internal Stress Evolution and Microstructural Feature

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Investigation of Cyclic Deformation Behavior in the Surface Layer of 18cr–8ni Austenitic Stainless Steel Based on Vickers Microhardness Measurement

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Dynamic strain ageing of austenitic Ni-based alloy during cyclic loading at 350 °C: Mechanism and its evolution

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Molecular dynamics study of fatigue mechanical properties and microstructural evolution of Ni-based single crystal superalloys under cyclic loading

The Dependence of Stress and Strain Rate on the Deformation Behavior of a Ni‐based Single Crystal Superalloy at 1050°C

Cyclic Deformation Behavior of Steels with a Nanolamellar Microstructure and Tensile Strength of 1500 MPa

Cyclic Deformation Behavior and Microstructure Evolution of High-Carbon Nano-Bainitic Steel at Different Tempering Temperatures

A Study of the Internal Deformation Fields and the Related Microstructure Evolution during Thermal Fatigue Tests of a Single-Crystal Ni-Base Superalloy

Cyclic deformation mechanism and fracture behaviour of 316L stainless steel under thermomechanical fatigue loading

Cyclic Deformation Behavior of a New N+C Alloying Austenitic Manganese Steel

Cyclic Deformation Behavior of a Nickel-Base Superalloy under Fatigue Loading

Cyclic Hardening and Dynamic Strain Aging During Low-Cycle Fatigue of Cr-Mo Tempered Martensitic Steel at Elevated Temperatures

Influence of time and temperature dependent processes on strain controlled low cycle fatigue behavior of alloy 617

Deformation mechanisms in a TiNi shape memory alloy during cyclic loading

Cyclic behavior and damage mechanism of 304 austenitic stainless steel under different control modes