Impact of a precise pH value change on the characteristics of deposited tin monosulphide films onto a flexible substrate

Noor M. Ibrahim,Manal M. Abdullah,Mohamed S. Mahdi

DOI: https://doi.org/10.1016/j.optmat.2023.114789

IF: 3.754

2024-01-03

Optical Materials

Abstract:The chemical bath deposition technique (CBD) is considered the cheapest and easiest compared with other deposition techniques. However, it is highly sensitive to effective parameter deposition values such as pH, temperature, and so on. The pH value of the reaction solution has a direct impact on both the nucleation and growth rate of the film. Consequently, this study presents a novel investigation into the effect of a precise change in the pH reaction solution value on the structural, morphological, and photoresponse characteristics of tin monosulphide (SnS) films. The films were grown on a flexible polyester substrate with pH values of 7.1, 7.4, and 7.7. The X-ray diffraction patterns of the grown films at pH 7.1 and 7.4 confirmed their polycrystalline nature. Additionally, an observed alteration in the crystal structure occurred as the pH value increased from 7.1 to 7.4, resulting in a transition from an orthorhombic crystal structure to a cubic crystal structure. In contrast, the XRD pattern of the grown film at pH 7.7 revealed that it was amorphous. The field-emission scanning electron microscopy images revealed a flower-like morphology for the grown film at 7.1, whereas the grown films at 7.4 and 7.7 revealed a grain morphology. The results also showed that the pH values were also having an important effect on the energy gap value ( Eg ) of films; the Eg values were 1.46, 1.57, and 1.65 eV for pH 7.1, 7.4, and 7.7, respectively. The photodetectors fabricated using grown films exhibited excellent photoresponse characteristics when subjected to near-infrared (750 nm) illumination. It was also demonstrated that the photodetector using the cubic structure film possessed faster response times and greater sensitivity than the photodetector using the orthorhombic structure film.

materials science, multidisciplinary,optics