In Situ Formation of MoS2 on the Surface of CF to Improve the Tribological Properties of PUE

Cunao Feng,Yu Guo,Xiaowei Li,Yang Cao,Qiuxue Kuang,Minghui Zhang,Dekun Zhang

DOI: https://doi.org/10.3390/ma16175773

IF: 3.4

2023-08-24

Materials

Abstract:The roller is an important part of the belt conveyor used in coal transportation. Due to the harsh environment of coal mines, the rollers are in a state of high load and high friction for a long time, which causes wear failure and has a serious impact on the reliability and safety of the equipment. In order to prepare roller material with excellent bearing performance and friction performance, CF/PUE composites were prepared by pouring method with polyurethane as the matrix and carbon fiber as reinforcement. Due to the low surface activity of unmodified carbon fibers and poor bonding performance with the matrix, MoS2 was generated on the surface of carbon fiber by the in situ generation method in this paper. It was found that the mechanical properties of MoS2/CF/PUE composites were better when the CF content was 0.3 wt%. The Shore hardness reached 92.2 HA, which is 10% higher than pure polyurethane. The tensile strength was 38.44 MPa, which is 53% higher than pure polyurethane. The elongation at break was 850%, which is 16% higher than pure polyurethane. The maximum compressive stress was 2.32 MPa, which is 42% higher than pure polyurethane. The friction coefficient was much lower than that of pure PUE composites, the friction coefficient was 0.284, which is 59% lower than pure polyurethane.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper attempts to address the issue of wear on roller materials used in coal transportation under harsh environments. Specifically, the rollers in coal transportation are subjected to high loads and high friction for extended periods, leading to wear failure, which severely affects the reliability and safety of the equipment. To prepare roller materials with excellent load-bearing and frictional performance, researchers used polyurethane (PUE) as the matrix and carbon fiber (CF) as the reinforcement material. They generated molybdenum disulfide (MoS2) in situ on the surface of the carbon fiber to improve the mechanical and tribological properties of the composite material. Through this method, the researchers aim to enhance the hardness, tensile strength, elongation at break, maximum compressive stress, and reduce the friction coefficient of the composite material. Experimental results show that when the CF content is 0.3 wt%, the MoS2/CF/PUE composite material exhibits the best mechanical properties.