Abstract:Aerogel has been widely known as a low-density and highly porous material and is closely connected with the complex processing methods, such as freeze–drying or supercritical drying. In this work, using the polymerization-induced aramid nanofiber (PANF) as a building block, we put forward a modified freezing–drying method for the high-efficiency preparation of all-<i>para</i>-aromatic-amide aerogels. In the preparation process, PANF hydrogel is first frozen at −18 °C and then dried at 20–150 °C for the formation of PANF aerogel. The PANF framework formed during the freezing process is crucial for the formation of the PANF aerogel. Moreover, the space-occupying effect of ice crystals is also helpful for the formation of the macroscopic pore structure in the aerogel. Aerogels with large size or well-controlled shape could be successfully obtained by this method. Through the variation of PANF concentration in the hydrogel and drying temperature, aerogels with different densities (20–185 mg/cm<sup>3</sup>) could be achieved, and the lowest density is reached at 150 °C, with the PANF concentration of 0.7%. The low-density PANF aerogels show high specific compressive strengths and low thermal conductivities, which are comparable to those resulting from the freeze–drying or supercritical drying method. Furthermore, the shrinkage phenomenon in the drying process could be skillfully utilized for the preparation of PANF aerogel-coated objects. The PANF aerogels could be applied as a thermal insulating material or shock absorption material in practical applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c01551?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c01551</a>.Figure S1–S16: statistics of the diameter of PANFs; repeated filtering-dispersing process and PANF hydrogels with different PANF concentration; different products obtained from different methods; macroscopic state of PANF hydrogel and thawed PANF hydrogel before and after magnetic stirring; PANF hydrogel and the corresponding PANF aerogel in the shape of mooncake; preparation process of PANF aerogel-coated quartz tube; SEM images of different PANF aerogels at a low (×50) and high (×50000) magnification; high-temperature (150 °C) drying experiment for unfrozen and frozen PANF hydrogels with PANF% = 0.7%; specific strength of different PANF aerogel samples (ε = 70%); specific strength comparison of PA-20 and PA-40 with the low-density ANF-based aerogels (ε = 30%); compressive stress–strain curves of PA-20 at different strains for 100 compression–decompression cycles; surface of PANF aerogel before and after heating by infrared ray bulb; temperature variations of water in the metal tubes (with or without PANF aerogel insulation layer) after heating by infrared ray bulb; profiles of PANF aerogel and PU foam in the hot stage heating test; TGA and DTA curves of PANF aerogel and PU foam in air atmosphere; Tables S1–S3: stress retention and height recovery rates of PA-20 after 100 compression–decompression cycles at different strains; thermal conductivities of PANF aerogels and the already reported aramid aerogels; specific strengths (ε = 70%) and thermal conductivities of different kinds of aerogels (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c01551/suppl_file/nn1c01551_si_001.pdf">PDF</a>)Movie S1: Drop test of the PANF aerogel-coated quartz tube (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c01551/suppl_file/nn1c01551_si_002.avi">AVI</a>)This article has not yet been cited by other publications.

Laminated aramid nanofiber aerogel reinforced epoxy resin composite

Functionalized Aramid Nanofibers Prepared by Polymerization Induced Self-Assembly for Simultaneously Reinforcing and Toughening of Epoxy and Carbon Fiber/epoxy Multiscale Composite

Rapid and Scalable Synthesis of Novel Carboxylated Aramid Nanofibers for Simultaneously Improving the Strength and Toughness of Carbon Fiber/epoxy Laminates

Effects of aramid nanofibers on the mechanical properties of epoxy resin and improved adhesion with aramid fiber

Flexible and Compressible Nanostructure-Assembled Aramid Nanofiber/Silica Composites Aerogel

Robust and Highly Resilient Waterborne Polyurethane-Based Composite Aerogels Prepared by Blending with Aramid Nanofibers

Preparation of carbon fibre-reinforced composite panels from epoxy resin matrix of nano lignin polyol particles

Preparation of highly active aramid fiber and effect on the interface property of aramid/epoxy composites

Enhancement of Para-Aramid Fibers by Depositing Poly-P-paraphenylene Terephthalamide Oligomer Modified Multi-Walled Carbon Nanotubes

Macroscopic-Scale Preparation of Aramid Nanofiber Aerogel by Modified Freezing–Drying Method

The Aramid-Coating-on-Aramid Strategy toward Strong, Tough, and Foldable Polymer Aerogel Films

Construction of Aramid Engineering Materials Via Polymerization‐Induced Para‐aramid Nanofiber Hydrogel

Large-area ultrastrong and stiff aramid nanofiber based layered nanocomposite films

Investigation of the thermal and tribological properties of epoxy composite reinforced with aramid nanofiber/OMMT hybrid aerogel

Preparation of aramid nanofiber and its application in polymer reinforcement: A review

Preparation and application of aramid nanofiber via carbodiimide assisted polymerization

Surface-modified alumina nanoparticles-filled aramid fiber-reinforced epoxy nanocomposites: preparation and mechanical properties

A Synergistic Strategy for Fabricating an Ultralight and Thermal Insulating Aramid Nanofiber/polyimide Aerogel

Carbon fiber reinforced carbon aerogel composites for thermal insulation prepared by soft reinforcement

Non-destructive modification of aramid fiber by building nanoscale-coating solution to enhance the interfacial adhesion properties of the fiber-reinforced composites

From Monomers to a Lasagna-like Aerogel Monolith: an Assembling Strategy for Aramid Nanofibers.