Abstract:<p>In this study, the microstructure evolution and mechanical anisotropy of the extruded Mg-2Zn-0.4Mn-0.4Ce alloy tube during tensile loading along the extrusion direction (ED), 45° towards extrusion direction (45°ED) and transverse direction (TD) were investigated, respectively. The results showed that the initial extruded alloy tube had an obvious {0001} basal fiber texture with the symmetrical pole position deviating about 20° from the RD to ED, which resulted in mechanical anisotropy of the tensile yield stress (TYS) when tensile loading along the ED, 45°ED and TD. The deformation behavior of the alloy tube consisted of three stages. In the yield process, the deformation was dominated by prismatic<a>slip under tensile loading along the ED, while the deformation was dominated by basal<a>slip, next were prismatic<a>slip and pyramidal<c+a>slip under tensile loading both along the 45°ED and TD. In the initial stage after yielding, some extension twin (ETW) formed when tensile loading along the three direction, and the deformations were still dominated by the previous slip systems. In the later part of the deformation, the activation of prismatic<a>slip and the nucleation and expansion of ETW gradually reached saturation under tensile loading along the ED. The dominated prismatic<a>slip was gradually replaced by pyramidal<c+a>slip, and accompanied with a small content of contraction twin (CTW) and double twin (DTW), thus forming a typical texture of [0001]⊥ED. For the deformation both along the 45°ED and TD, dominated prismatic<a>slip and subdominant pyramidal<c+a>slip gradually became the main deformation mode after the saturation of basal<a>slip and ETW, and a small content of CTW and DTW also formed, thus forming the texture of [0001]∥ED-RD plane.</a></c+a></a></c+a></a></a></c+a></a></a></a></p>

<i>In</i>-<i>situ</i> investigation on the microstructure evolution of Mg-2Gd alloys during the V-bending tests

Anomalous effect of grain size on the room-temperature bendability of Mg–Gd alloy sheet

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Finite Element Simulation and Experiment on the Microstructure of High-Strength Mg-Gd-Y-Zn-Zr Alloy during U-Shaped Bending Process

In-situ EBSD analysis of microstructural evolution and damage behavior of Mg-Al-Ca-Mn alloys with different extrusion ratios

Microstructure Evolution and Mechanical Behavior of AZ31 Magnesium Alloy Sheet with Bimodal Texture under Bending Deformation

Quasi-in-situ observations of microstructural evolution during cyclic deformation of a Mg-Zn-Ca alloy

On the inhomogeneous deformation behavior of magnesium alloy beam subjected to bending

The effect of cross-section geometry of castings on dendrite evolution in Mg Gd alloys by in situ X-ray radiography

Mechanical responses and deformation mechanisms in the AZ31 magnesium alloy during cyclic bending

Study on the microstructure changes during the in situ tensile processes of as-cast and aged specimens of high-vacuum die-cast Mg-9Al-1Zn alloy

In-situ and ex-situ investigation of deformation behaviors of a dual-phase Mg−Ni−Y alloy

Microstructure evolution difference in Mg96.5Gd2.5Zn1 alloys extruded from as-cast and solution-treated states

Microstructure Evolution and Deformation Behavior of Extruded Mg-5Al-0.6Sc Alloy during Room and Elevated Temperature Tension Revealed by Ex-Situ EBSD and VPSC

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Deformation mechanism of high ductility Mg-Gd-Mn alloy during tensile process

The Effect of Gd and Zn Additions on Microstructures and Mechanical Properties of Mg-4sm-3nd-Zr Alloy

The microstructure evolution and mechanical anisotropy of extruded Mg-2Zn-0.4Ce-0.4Mn alloy tube during tension in different directions

Deformation Mechanisms of Magnesium Alloys with Rare-Earth and Zinc Additions under Plane Strain Compression

A comparative study of deformation behaviors and ductility improvement in Mg–Gd–Zr and Mg–Zr cast alloys