Nucleation and Growth of Nanoscale Precipitates and the Effect on Properties During Secondary Isothermal Aging in Thin-Band of Cu–0.8Cr–0.1Zr Alloy

Zhiguo Wang,Guangming Cao,Weina Zhang,Chengang Li,Zhenyu Liu

DOI: https://doi.org/10.1016/j.mtla.2022.101452

2022-01-01

Materialia

Abstract:The precipitation behavior during secondary isothermal aging of Cu-0.8Cr-0.1Zr alloy, especially the nucleation and growth of nanoscale body-centered cubic (bcc) Cr and orthogonal Cu4Zr precipitates, were clarified through high-resolution crystal structure and atomic-scale composition analysis. Results demonstrated that the crystal nucleus of face-centered cubic (fcc) Cr and fcc Zr would be preferentially precipitated in a coherent orientation relationship (OR) with fcc Cu-based matrix. As they grew up, fcc Cr gradually developed into stable bcc structure, and the OR with matrix changed from N-W to incoherent. While fcc Zr would change lattice constant by atomic diffusion and segregation to evolve into stable Cu4Zr with orthogonal structure, during which they were precipitated on the Cu-Cr-Zr solid solution through a process of discharging surrounding Cr atoms. Abundant dispersed nanoscale precipitates that induced by the secondary aging contributed to produce well-matched comprehensive properties (sigma(b )= 669 MPa, I = 84.3 %IACS).