Plastic Deformation Behavior of Mg-Li Alloys at Ambient and Elevated Temperatures
Wei Tang,Yujie Xu,En–Hou Han
DOI: https://doi.org/10.4028/www.scientific.net/msf.488-489.531
2005-01-01
Materials Science Forum
Abstract:The deformation behavior of three kinds of Mg-Li alloys with different test conditions at ambient and elevated temperatures was studied, and the optimized deformation conditions were obtained. The results showed that the addition of lithium increases the plasticity, but little bit decreases in strength of the alloy. However, the strength may be enhanced through the addition of aluminum into the alloy due to the phase precipitation in the alloy matrix. It is also found that elongation depends mainly on both test temperature and strain rate, and the maximum elongation occurs at 350 and 5×10 -4 s -1 for α-alloy, 350 and 5×10 -4 s -1 for β-alloy, and 400 ,5×10s for α+β alloy. Further study revealed that the dual-phase α+β alloy exhibited superplastic deformation behavior at a certain condition under which the structures were refined and the texture was disappeared. Introduction Magnesium lithium alloys have potential for use in aerospace applications because they are exceptionally light and their specific stiffness is high. The addition of lithium into magnesium, it makes magnesium-lithium alloy not only become the lightest alloy, offering density comparable to engineering plastics, but also change the crystal structure of the alloys [1,2] . When the content of Li in the matrix is higher than 5.5wt%, the β-phases with bcc structure begins to precipitate in the solid solution, consisting of the hcp α-phase and bcc β-phase. When the addition of Li is over 10.3wt%,the alloy is transformed intoβ-alloy completely. As increasing in Li, the crystal lattice axes ratio, a/c, decreases through substitution of Mg atoms by Li atoms [5,6] . The reduction of the atomic distances lead to the decrease in activation energy in hcp crystal needed for prismatic slip system, and this further results to the improvement in plasticity, and even super-plasticity to occur at certain conditions [7-9] . The general mechanical properties of Mg-Li alloys have been extensively investigated (3-12) . However there has been little work reported on the deformation mechanism of Mg-Li alloys at elevated temperature. This paper presents an investigation of deformation behavior of three-kinds of Mg-Li alloys. Materials and Procedure Three-kinds of the Mg-Li alloys were prepared by vacuum casting under a protective atmosphere of Argon. The ingots were then homogenized at 350 o C for 24h, followed by conventional extruded at 300 o C into the alloy sheets. Their chemical compositions (wt.%) are listed in Table 1. Table 1 Chemical compositions (wt.%) of the alloys tested Alloys structure Li Al Mg α-alloy HCP 3.3 Bal. α+βalloy HCP+BCC 8.5 1 Bal. β-alloy BCC 14.1 1 Bal. Materials Science Forum Online: 2005-07-15 ISSN: 1662-9752, Vols. 488-489, pp 531-534 doi:10.4028/www.scientific.net/MSF.488-489.531 © 2005 Trans Tech Publications Ltd, Switzerland All rights reserved. No part of contents of this paper may be reproduced or transmitted in any form or by any means without the written permission of Trans Tech Publications Ltd, www.scientific.net. (Semanticscholar.org-11/03/20,11:32:30) Results and Discussion Stress-strain response at ambient temperature Fig.1 shows the stress-strain response, and Table 2 gives main mechanical properties of the alloys at room temperature. 0.00 0.05 0.10 0.15 0.20 0 50 100 150 200 250 300 β alloy α+β alloy α alloy S tr e n g th /M P a Strain 0.00 0.05 0.10 0.15 0.20 0.25 0.30 0 50 100 150 200