Abstract:Four highly rigid spirobifluorene polyimides are designed, and their optical properties are successfully regulated by small side groups and periodic distortions. These units enable well‐balanced thermal and optical properties in CPIs, with 27SPFTFA‐BPAF showing optimal performance (Tavg = 86%, YI = 3.53, Tg = 422 °C, CTE = 35 ppm K−1, δmax = 140 MPa). Advancements in flexible electronic technology, especially the progress in foldable displays and under‐display cameras (UDC), have created an urgent demand for high‐performance colorless polyimide (CPI). However, current CPIs lack sufficient heat resistance for substrate applications. In this work, four kinds of rigid spirobifluorene diamines are designed, and the corresponding polyimides are prepared by their condensation with 5,5′‐(perfluoropropane‐2,2‐diyl) bis(isobenzofuran‐1,3‐dione) (6FDA) or 9,9‐bis(3,4‐dicarboxyphenyl) fluorene dianhydride (BPAF). The rigid and conjugated spirobifluorene units endow the polyimides with higher glass transition temperature (Tg) ranging from 356 to 468 °C. Their optical properties are regulated by small side groups and spirobifluorene structure with a periodically twisted molecular conformation. Consequently, a series of CPIs with an average transmittance ranging from 75% to 88% and a yellowness index (YI) as low as 2.48 are obtained. Among these, 27SPFTFA‐BPAF presents excellent comprehensive performance, with a Tg of 422 °C, a 5 wt.% loss temperature (Td5) of 562 °C, a YI of 3.53, and a tensile strength (δmax) of 140 MPa, respectively. The mechanism underlying the structure‐property relationship is investigated by experimental comparison and theoretical calculation, and the proposed method provides a pathway for designing highly rigid conjugated CPIs with excellent thermal stability and transparency for photoelectric engineering.

Super-heat resistant, transparent and low dielectric polyimides based on spirocyclic bisbenzoxazole diamines with <i>T</i><sub>g</sub> > 450 C

Super-heat resistant, transparent and low dielectric polyimides based on spirocyclic bisbenzoxazole diamines with Tg > 450 °C

High Tg, Low Dielectric, and Colorless Transparent Polyimides Based on Rigid 9,9-Spirobixanthene Diamines

Synthesis of highly transparent and heat-resistant polyimides containing bulky pendant moieties: Synthesis of highly transparent and heat-resistant polyimides containing bulky pendant moieties

Heat-resistant Colorless Polyimides from Benzimidazole Diamines: Synthesis and Properties

Colorless transparent and thermally stable terphenyl polyimides with various small side groups for substrate application

Thermally Stable and Transparent Polyimide Derived from Side‐Group‐Regulated Spirobifluorene Unit for Substrate Application

Synthesis and Characterization of Organo-Soluble Polyimides Based on Polycondensation Chemistry of Fluorene-Containing Dianhydride and Amide-Bridged Diamines with Good Optical Transparency and Glass Transition Temperatures over 400 °C

Intrinsic Low-Dielectric Cardo Polyimide with High Heat Resistance, High Transparency, and Low Birefringence

Heat‐resistant and transparent polyimides derived from alicyclic dianhydrides and phthalazinone‐based diamine

Synthesis and properties of novel colorless and thermostable polyimides containing cross‐linkable bulky tetrafluorostyrol pendant group and organosoluble triphenylmethane backbone structure

Terphenyl-based Colorless and Heat-resistant Polyimides with Controlled Molecular Structure by Methyl Side Groups

Synthesis and Characterization of Thioether-Containing Polyimides with High Refractive Indices

High Glass Transition Temperature and Ultra‐low Thermal Expansion Coefficient Polyimide Films Containing Rigid Pyridine and Bisbenzoxazole Units

Synthesis and comparative study of high Tg and colorless polyamide‐imides with different amide‐to‐imide ratio

High Performance Transparent Polyimides by Controlling Steric Hindrance of Methyl Side Groups

Design, Synthesis and Properties of Semi-Alicyclic Colorless and Transparent Polyimide Films with High Glass Transition Temperatures and Low Retardation for Potential Applications in Flexible Electronics

Optically Transparent and Thermal‐Stable Polyimide Films Derived from a Semi‐Aliphatic Diamine: Synthesis and Properties

Cardo polyimides with high Tg and transparency derived from bisphenol fluorenes and 1,4-bis(4-fluorophthalimide)cyclohexanes via aromatic nucleophilic substitution

Soluble and Transparent Polyimides with High Tg from a New Diamine Containing Tert‐butyl and Fluorene Units

Soluble And Transparent Polyimides With High T-G S From A New Semi-Aliphatic Diamine With Cyclohexyl And Ortho-Methyl Groups