Phase separation of chemically crosslinked poly(<i>n</i>-butyl methacrylate-co-methacrylic acid) in mixtures of <i>N,N</i>-dimethyl formamide and water

Chuhao Qiu,Weixiang Sun,Tao Wang,Zhen Tong

DOI: https://doi.org/10.1016/j.polymer.2022.125009

IF: 4.6

2022-01-01

Polymer

Abstract:When a copolymer network of chemically crosslinked poly(n-butyl methacrylate-co-methacrylic acid) was immersed into a bath of N,N-dimethylformamide (DMF) and water, the swollen network underwent phase separation depending on the fraction xw of water in the bath. Swelling ratio, light transmittance, thermomechanics, dynamical mechanical spectra, and tensile property of the gels in baths of different xw's were investigated. A ternary phase diagram of this system was calculated from theory for comparison of the experimental data. A glass line was also provided in the ternary phase diagram from the estimation by the diluent effect on glass temperature. The results indicated that the polymer-rich phase after phase separation became glassy as the bath composition xw was above 0.75. This resulted in a fundamental change in the thermomechanical behavior of the gel from one of a typical rubber to one a typical glassy polymer. Meanwhile a dynamical gel-to-glass transition was observed in the time-temperature superposition (TTS) master curves. The transition temperature T0 decrease with increasing xw. A weak-to-tough transition was observed at T -T0 & AP;0 K, while a tough-to-brittle transition occurs at T -T0 & AP;-50 K. A conceptual scheme was proposed to clarify the interplay of phase separation, glass transition in the present work. This scheme could also explain some of the previous work. An example of application in shape memory materials was provided.