Abstract:Haynes 230 alloy is widely used in gas turbine engines, because of its high strength, fatigue, and oxidation resistance. Nevertheless, studies on the hot crack inhibition, strengthening and toughening mechanisms of Haynes 230 alloy manufactured by laser powder bed fusion are limited. Hence, this study investigates the proposed process parameter and scanning strategy synergistic control defect, microstructure, and mechanical properties of Haynes 230 alloy fabricated by laser powder bed fusion . Also, this study discusses the hot crack inhibition, enhanced strength and ductility mechanism. The relationship between volumetric laser energy density and scanning strategy to the relative density was established. It was found that many sub-grains are present in molten pool, which are cellular and columnar dendrites. A large number of nanoprecipitates (M 23 C 6 , rich La) were precipitated on the grain boundaries and matrix, with the following orientation relationship:[011] Î³ //[011] M23C6. Unmelted voids, pores, and hot cracks were further clarified as types of defects. However, emphasis was made on identifying the hot crack nucleation and expansion mechanisms. The liquid film, low-melting eutectic phase, and high angle grain boundaries promoted crack nucleation. Precipitation phases produce large hot stresses, hot stresses provide the motive forces for crack nucleation and extension. This is due to the elimination of hot stress concentration, grain refinement, and columnar to equiaxed transition using a low volumetric laser energy density and reasonable scanning strategy method. Meanwhile, the optimized parts exhibit simultaneously excellent strength and ductility with yield strength, tensile strength, and ductility of ~604 MPa, ~975.46 MPa and ~38.94 %, respectively. The enhancement of ductility for Haynes 230 alloy was mainly synergistic effect inhibition of porosity and cracks, grain refinement, and nanoprecipitates, whereas strengthening mechanisms is due to the synergistic effect of grain strengthening, Orowan strengthening, load strengthening, and nano-twinned strengthening.

Laser Powder Bed Fusion of Haynes 230 Superalloy: Microstructure, Mechanical Properties and Hot Cracking Inhibition

Simultaneous regulation of strength and ductility of laser powder bed fusion manufactured Haynes 230 alloy

Mechanical Properties and Fracture Behavior of Laser Powder-Bed-Fused GH3536 Superalloy

A high-strength Ni–Cr–W based superalloy prepared by laser powder bed fusion: printability, microstructure and tensile properties

Study of the Printability, Microstructures, and Mechanical Performances of Laser Powder Bed Fusion Built Haynes 230

The role of ceramic particles on the crack inhibition and mechanical properties improvement of Haynes 230 alloy fabricated by laser powder bed fusion

High-temperature Oxidation Behavior of AlCoCrCuFeNi High-Entropy Alloy by Selective Laser Melting

Additively manufactured crack-free nickel-based superalloys with synergistic strength and plasticity via grain refinement and striped oxides inhibition

Microstructure, crack formation and improvement on Nickel-based superalloy fabricated by powder bed fusion

Significantly improved weldability in laser welding of additively manufactured Haynes 230 superalloys by tailoring microstructure

Strengthening mechanism of a Ni-based superalloy prepared by laser powder bed fusion: The role of cellular structure

Significant reduction of grain size and texture intensity in laser powder bed fusion fabricated nickel-based superalloy by increasing constitutional supercooling

A precipitation strengthened high entropy alloy with high (Al+Ti) content for laser powder bed fusion: Synergizing in trinsic hot cracking resistance and ultrahigh strength

Reducing cracking sensitivity of CM247LC processed via laser powder bed fusion through composition modification

Microstructural Evolution and Formation of Fine Grains During Fatigue Crack Initiation Process of Laser Powder Bed Fusion Ni-based Superalloy

ICME framework to simulate microstructure evolution during laser powder bed fusion of Haynes 282 nickel-based superalloy

Micro-cracking, microstructure and mechanical properties of Hastelloy-X alloy printed by laser powder bed fusion: As-built, annealed and hot-isostatic pressed

Solidification Track Morphology, Residual Stress Behavior, and Microstructure Evolution Mechanism of FGH96-R Nickel-Based Superalloys during Laser Powder Bed Fusion Process

Crack Inhibition and Performance Modification of NiCoCr-Based Superalloy with Y2O3 Nanoparticles by Laser Metal Deposition

High-temperature high cycle fatigue performance of laser powder bed fusion fabricated Hastelloy X: Study into the microstructure and oxidation effects

Laser powder bed fusion of nano-titania modified 2219 aluminium alloy with superior mechanical properties at both room and elevated temperatures: The significant impact of solute