A Mixed-Potential Type NH ₃ Sensor Based on Spinel Zn ₂SnO ₄ Sensing Electrode

Yu Zhang,Yongguang Liu,Ling Wang,Huizhu Zhou,Weiwei Meng,Yuehua Li,Zhangxing He,Lei Dai

DOI: https://doi.org/10.2139/ssrn.4009450

2022-01-01

Abstract:Spinel oxide Zn2SnO4 with cubic structure was synthesized by solid state reaction way. A NH3 sensor based on the mixed potential mechanism was fabricated with Yttria stabilized zirconia (YSZ) electrolyte and Zn2SnO4 sensing electrode (SE). The influence of Zn2SnO4-SEs sintering temperature on the response performance of the sensor was evaluated. The different NH3 sensors were prepared by sintering Zn2SnO4-SE at 1000 °C, 1100 °C and 1200 °C and the experimental results display that among all sensors the sensor using Zn2SnO4-SE sintered at 1100 °C gives the highest sensitivity of -61.2 mV/decade with an operating temperature of 600 °C, which is closely related to the microstructure of the Zn2SnO4-SE by SEM analysis. The sensor response signals linearly depend on the logarithm of NH3 concentrations in the range of test temperature. The sensor based on Zn2SnO4-SE sintered at 1100 °C shows the best performance at 600 °C. The polarization curve and Tafel plots verify that the sensor complies with the mixed potential model. The cross-sensitivity experiment results show the NH3 sensitivity decreases with the increasing of O2 content. The cross-sensitivity of the sensor towards CO2 and H2 is hardly observed, but NO and NO2 cause serious interference which needs to be overcome in the future work. The sensor also shows a relatively good repeatability and long-term stability.