Luminescence and Stability Enhancement of CsPbBr 3 Perovskite Quantum Dots through Surface Sacrificial Coating
Dong Huang,Jun Bo,Ronghong Zheng,Chengzhao Luo,Xiaojuan Sun,Qinyi Li,Dongyang Shen,Zhishuai Zheng,Mengyu Chen,Yixing Yang,Aiwei Tang,Song Chen,Yu Chen
DOI: https://doi.org/10.1002/adom.202100474
IF: 9
2021-05-18
Advanced Optical Materials
Abstract:<p>All‐inorganic perovskite quantum dots (QDs) have emerged as a new category of low‐cost semiconducting luminescent materials for optoelectronic applications. However, their poor stability has become the main challenge that impedes their potential applications. Herein, Ni‐doped CsPbBr<sub>3</sub> QDs with lead phosphate (Pb<sub>3</sub>(PO<sub>4</sub>)<sub>2</sub>) shell through surface sacrificial coating (c‐Ni‐CsPbBr<sub>3</sub>) have been developed based on a modified thermal injection approach. The synergistic effect of Ni doping and Pb<sub>3</sub>(PO<sub>4</sub>)<sub>2</sub> coating effectively improves the stability and optical performances of CsPbBr<sub>3</sub> QDs, including photoluminescence (PL) intensity, the average lifetime, and PL quantum yield (QY). Thus, the c‐Ni‐CsPbBr<sub>3</sub> QDs demonstrate the full width at half maxima (FWHM) and PLQY being 18.42 nm and 90.77%, respectively. The PL intensity of c‐Ni‐CsPbBr<sub>3</sub> can be maintained at 81% of its original value after being heated at 100 °C for 1 h. No phase transformation can be observed after being stored under ambient conditions (25 °C, 60% relative humidity (RH)) for 21 days. In addition, by combining green c‐Ni‐CsPbBr<sub>3</sub> QDs, red CdSe‐based QDs and the blue GaN chip, a QD enhancement film (QDEF) is fabricated to form a liquid crystal display (LCD) backlit with a wide color gamut covering cover 121% of the National Television System Committee (NTSC) standard.</p>
materials science, multidisciplinary,optics