Stability and photocurrent enhancement of photodetectors by using core/shell structured CsPbBr3/TiO2 quantum dots and 2D materials

Chathurika Maduwanthi,Chao-An Jong,Waleed S. Mohammed,Shu-Han Hsu
DOI: https://doi.org/10.1039/d3na01129a
IF: 5.598
2024-04-03
Nanoscale Advances
Abstract:Ultra-stable CsPbBr 3 perovskite quantum dots (QDs) were prepared, and the performance of the photodetector fabricated from them was enhanced by 2D material incorporation. This multi-component photodetector appears to have good stability in the ambient utilization environment. All inorganic CsPbBr 3 QDs are potential candidates for application in photodetection devices. However, QDs have several issues such as defects on the QD surface, degradation under environmental conditions, and unfavorable carrier mobility limiting the high performance of the photodetectors. This work addresses these issues by fabricating a core/shell structure and introducing 2D materials (MXenes, Ti 3 C 2 T x ) into the device. Here, three types of photodetectors with QDs only, QDs with a core/shell structure, and QDs with a core/shell structure and MXenes are fabricated for systematic study. The CsPbBr 3 /TiO 2 photodetector demonstrated a two times photocurrent enhancement compared to bare QDs and had good device stability after TiO 2 shell coating. After introducing Ti 3 C 2 T x into CsPbBr 3 /TiO 2 , a significant photocurrent enhancement from nanoampere (nA) to microampere (μA) was observed, revealing that MXenes can improve the photoelectric response of perovskite materials significantly. Higher photocurrent can avoid signal interference from environmental noise for better practical feasibility. This study provides a systematic understanding of the photocurrent conversion of perovskite quantum dots that is beneficial in advancing optoelectronic device integration, especially for flexible wearable device applications.
materials science, multidisciplinary,nanoscience & nanotechnology,chemistry
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to improve the stability and photocurrent performance of perovskite quantum dot (QDs) - based photodetectors (PDs). Specifically, by constructing a CsPbBr₃/TiO₂ core - shell structure and introducing two - dimensional materials MXenes (such as Ti₃C₂Tₓ), the researchers aim to solve the problems of perovskite quantum dots, such as easy degradation under environmental conditions, numerous surface defects and low carrier mobility. These problems limit the high - performance applications of photodetectors. Through these improvements, the researchers aim to generate a higher photocurrent, thereby avoiding the interference of environmental noise on the signal and improving the feasibility of practical applications, especially in the field of flexible wearable devices. ### Main problems to be solved: 1. **Stability problem**: Perovskite quantum dots are easily degraded under environmental conditions, resulting in poor long - term stability of the device. 2. **Photocurrent enhancement**: By constructing a core - shell structure and introducing 2D materials, the photocurrent of the photodetector is increased, thereby enhancing its performance. 3. **Carrier transport efficiency**: Reduce the loss of carriers during the transport process and improve the photoelectric conversion efficiency. ### Specific methods: - **Core - shell structure**: Use TiO₂ as the shell layer to wrap CsPbBr₃ quantum dots, forming a CsPbBr₃/TiO₂ core - shell structure to improve the stability of the quantum dots. - **Introduction of 2D materials**: On the basis of the core - shell structure, further introduce MXenes (such as Ti₃C₂Tₓ) to improve the carrier transport efficiency and significantly increase the photocurrent. ### Experimental results: - **Photocurrent enhancement**: Compared with pure CsPbBr₃ quantum dots, the photocurrent of the CsPbBr₃/TiO₂ core - shell structure is doubled. After the introduction of MXenes, the photocurrent is further significantly increased, reaching 40,000 times. - **Responsivity and detectivity**: The responsivity and detectivity of CsPbBr₃/TiO₂/MXene PD are 3,696 A/W and 7.6 × 10¹⁴ Jones respectively, which are much higher than those of other types of photodetectors. ### Conclusion: By constructing a CsPbBr₃/TiO₂ core - shell structure and introducing MXenes, the stability and photocurrent performance of photodetectors can be significantly improved. This research provides new ideas and technical support for the application of integrated optoelectronic devices, especially flexible wearable devices. Future research can further explore the introduction of other conductive materials to optimize the effect of multi - component mixing.