Abstract:Stereolithography based-3D printing technology requires ceramic slurries with high solid content and low viscosity to prevent the formation of cracks, holes, warping, and other defects in sintered ceramic parts. In this study, several approaches based on optimization of alumina powder and coupling agent were explored to improve the solid content of ceramic slurries. It was shown that slurries containing γ-Al2O3 reached solid content of only 22.5 wt% and viscosity of 15,199 mPa·s. By comparison, slurries composed of α-Al2O3 reached higher solid content of 75 wt% and viscosity of 12,780 mPa·s. Three types of coupling agents, namely (3-Aminopropyl) triethoxysilane, (Aminoethylamino) propyldimethoxymethylsilane and 3-(Trimethoxysilyl) propyl methacrylate (abbreviated as E, F and G, respectively) were used to reduce the viscosity of the slurries. The addition of 10 wt% G led to slurry solid content reaching 82 wt% and viscosity of 860 m·Pas. The significant decrease in viscosity was mainly attributed to the presence of bifunctional hydrolyzable groups in G, which could well attach to alumina. On the other hand, the presence of organo-functional groups might also well attach to the photosensitive resin. The ceramics prepared with γ-Al2O3 exhibited numerous pores in both intraparticle and intergranular while those obtained with α-Al2O3 showed pores in only intergranular. The porous structure in γ-Al2O3 occupied large space, leading to low solid content. Ceramics prepared with 75 wt% solid content possessed flexural strength of 29.3 MPa, bulk density of 2.3 g/cm3 and open porosity of 39.8 %. By comparison, ceramics prepared with 82 % solid content showed flexural strength of 45.0 MPa. In sum, these findings look promising for future preparation of high-solid content 3D printed ceramic slurries for complex ceramics, such as ceramic cores.

Effect of Solid Loading on the Property of Al2O3 Ceramics in Stereolithographic Additive Manufacturing

Rheological behavior and curing deformation of paste containing 85 wt% Al2O3 ceramic during SLA-3D printing

Roles of solid loading in stereolithography additive manufacturing of ZrO<sub>2</sub> ceramic

High Solid Loading, Low Viscosity Photosensitive Al2O3 Slurry for Stereolithography Based Additive Manufacturing

3D Printed Ceramic Slurries with Improved Solid Content Through Optimization of Alumina Powder and Coupling Agent

Effect of synergism of solid loading and sintering temperature on microstructural evolution and mechanical properties of 60 vol% high solid loading ceramic core obtained through stereolithography 3D printing

Effects of Fine Grains and Sintering Additives on Stereolithography Additive Manufactured Al2O3 Ceramic

Investigating the effect of solid loading on microstructure, mechanical properties, and translucency of highly translucent zirconia ceramics prepared via stereolithography-based additive manufacturing

Effects of Solid Loading on Stereolithographic Additive Manufactured ZrO2 Ceramic: A Quantitative Defect Study by X-ray Computed Tomography

Effects of Particle Size and Color on Photocuring Performance of Si3N4 Ceramic Slurry by Stereolithography

A Comprehensive Study on Zirconia Slurry for Stereolithography-Based Additive Manufacturing

Effect of Solid Loading of Slurry on Properties of Si<sub>3</sub>N<sub>4</sub> Ceramics Formed by Digital Light Processing

Synergy of Solid Loading and Printability of Ceramic Paste for Optimized Properties of Alumina Via Stereolithography-Based 3D Printing

Rheology and Curability Characterization of Photosensitive Slurries for 3D Printing of Si3N4 Ceramics

Dynamic mechanical properties of Alumina prepared by vat photopolymerization based on high solid loading slurry

Preparation of silicon carbide ceramic slurry for stereolithography based additive manufacturing

Effect of solid loading on properties of zirconia ceramic by direct ink writing

Fabrication of alumina ceramics with high flexural strength using stereolithography

Fabrication and properties of alumina ceramics shaped by digital light processing as an additive manufacturing technology

Effects of Solid Loading in Initial Slurry on Microstructure and Properties of Porous Mullite Ceramics

Supportability of a High-Yield-Stress Slurry in a New Stereolithography-Based Ceramic Fabrication Process