Abstract:The class of NbC-Ni cermets has emerged as a promising environmentally friendly alternative to WC-Co cemented carbide tools, although some inherent properties i.e. room temperature hardness and flexural strength, of NbC-Ni cermets may require further enhancements. To enhance the properties of NbC-Ni cermets, diverse methodologies were applied, including grain inhibition and the strengthening of the cermet through the use of reinforcements. This study systematically examined the impact of TiC additions, specifically at 10% and 20%, on both the microstructure and mechanical properties of NbC-12Ni-4VC-4Mo2C cermets. NbC-12Ni cermets were fabricated via vacuum liquid phase sintering (LPS) at 1400°C and 1450°C. Enhancements by incorporating 4% VC and 4% Mo2C, followed by TiC at 10% and 20% concentrations to the NbC-Ni-4VC4Mo2C cermet were made. XRD and SEM results confirm the formation of (Nb, X, Y) C solid solution cubic FCC carbides. Significant grain refinement was evident in the cermet samples, subjected to grain inhibition. The observed grain sizes ranged from a maximum of 6.84 μm (in NbC12Ni) to a minimum of 2.154 μm (in the sample containing 20% TiC) at 1450°C. The incorporation of 20TiC at 1450°C led to a remarkable 26.5% enhancement in average hardness compared to NbC-Ni cermet, and a 4.2% improvement over the 4VC4Mo2C cermet. At 1450°C, 20TiC reinforcement led to an average fracture toughness of 9.331 MPa√m, representing a 4.56% improvement over the 4VC4Mo2C cermet. However, there was a marginal reduction in toughness compared to the NbC-Ni cermet. Moreover, the addition of TiC led to a decrease in the flexural strength of the cermets, with a maximum flexural strength of 939 N/mm2 recorded for NbC-Ni-4VC4Mo2C, representing an 11.6% increase compared to the NbC-Ni cermet.

Microstructure and Properties of Ti(C-x,N1-x)-based Cermets with Different C/N Ratios

Correlation between microstructure and mechanical properties of Ti(C,N)-xWC-Ni cermets prepared by mechanical activation and subsequent in situ carbothermal reduction

Effects of CrMnFeCoNi additions on microstructure, mechanical properties and wear resistance of Ti(C,N)-based cermets

Study on the growth and wear characters of CVD coating deposited on Ti(C, N)-based cermets with adding different C/N ratios of Ti(C, N) powders

Microstructure and Properties of Ti(C,N)-Based Cermets with AlxCoCrFeNiTi Binder

Effect of Cr2C3 addition on microstructure and mechanical properties of Ti(CN)-based cermets

Effect of Cr<sub>2</sub>C<sub>3</sub> Addition on Microstructure and Mechanical Properties of Ti(CN)-Based Cermets

Microstructure and properties of Ti(C, N)-based cermet with multi-core-rim microstructure: effect of (Ti, W, Ta) (C, N) pre-solid solution composition

Influence of TaC content on microstructure and mechanical performance of Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Microstructure and Mechanical Properties of TiC Reinforced NbC-Ni4VC4Mo2C Cermets

Improvement of microstructure, mechanical properties and cutting performance of Ti(C,N)-based cermets by ultrafine La2O3 additions

Submicron Ti(C,N)-based cermets with improved microstructure using high-energy milled and subsequent heat-treated ultrafine Ti(C,N) powders

Effect of Tic/Tin Powder Size on Microstructure and Properties of Ti(C, N)-Based Cermets

Nano TiC modified Ti(C,N)-based cermets with weakened rim-binder interfaces

Effect of diamond addition on microstructure and mechanical properties of Ti(C,N)-based cermets

Effect of C content on the surface gradient structure of (Ti, Mo)(C, N) and Ti(C, N)-based cermets

Microstructure, Interface Characteristics and Mechanical Properties of Ti(C,N)-based Cermets with a Cellular Structure

Influence of C and Al Addition on Microstructure and Mechanical Properties of Ultrafine TiCN-Based Cermets

Fabrication, microstructure evolution, and mechanical properties of Ti(C,N)-HfN-WC-Ni-Mo cermets

The production of in situ (Mo,Ti)(C,N)-based cermets without a core/rim structure by reaction hot pressing: Formation mechanism and mechanical properties

Strengthening and toughening of Ti(C,N)-based cermets: (Ti,W)C additive design and the mechanism