Abstract:This work investigates the possibility of using LaMn0.7Fe0.3O3.15@mSiO(2) as oxygen carriers for chemical looping combustion (CLC). CLC is a new combustion technique with inherent separation of CO, from atmospheric N-2. LaMn0.7Fe0.3O3.15@mSiO(2) core shell materials were prepared by coating a layer of mesostructured silica around the agglomerated perovskite particles. The oxygen carriers were characterized using different methods, such as X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), N-2 sorption, hydrogen temperature-programmed reduction (H-2-TPR), and temperature-programmed desorption of oxygen (TPD-O-2). The reactivity and stability of the carrier materials were tested in a special reactor, allowing for short contact time between the fluidized carrier and the reactive gas [Chemical Reactor Engineering Centre (CREC) fluidized riser simulator]. Multiple reduction oxidation cycles were performed. TEM images of the carriers showed that a perfect mesoporous silica layer was formed around samples with 4, 32, and 55 nm in thickness. The oxygen carriers having a core shell structure showed higher reactivity and stability during 10 repeated redox cycles compared to the LaMn0.7Fe0.3O3.15 core. This could be due to a protective role of the silica shell against sintering of the particles during repeated cycles under CLC conditions. The agglomeration of the particles, which occurred at high temperatures during CLC cycles, is more controllable in the core shell-structured carriers, as confirmed by SEM images. XRD patterns confirmed that the crystal structure of all perovskites remained unchanged after multiple redox cycles. Methane conversion and partial conversion to CO, were observed to increase with the contact time between methane and the carrier. Indeed, more oxygen from the carrier surface, grain boundaries, and even from the bulk lattice was released to react with methane. Upon rising the contact time, less CO was formed, which is desirable for CLC application. Increasing the reaction temperature and methane partial pressure lead to enhanced conversions of CH4 under CLC conditions.

Chemical Looping Steam Methane Reforming Using Al Doped LaMnO3+δ Perovskites As Oxygen Carriers

Enhanced Activity of La1-xMnCuxO3 Perovskite Oxides for Chemical Looping Steam Methane Reforming

Evaluation of Fe Substitution in Perovskite LaMnO3 for the Production of High Purity Syngas and Hydrogen

Chemical-looping Reforming of Methane over La-Mn-Fe-O Oxygen Carriers: Effect of Calcination Temperature

Development of Sinter-Resistant Core–Shell LaMnxFe1–xO3@mSiO2 Oxygen Carriers for Chemical Looping Combustion

Highly Active La0.35Sr0.35Ba0.3Fe1-xCoxO3 Oxygen Carriers with the Anchored Nanoparticles for Chemical Looping Dry Reforming of Methane

Oxygen activity regulation over LaNiO 3 perovskites by Ti substitution for chemical looping partial oxidation of methane

Oxygen Release and Reduction Kinetics of La0.35Sr0.35Ba0.3Fe1-xCoxO3 As Oxygen Carriers for Chemical Looping Dry Reforming of Methane

Lattice oxygen behaviors of Mn-based catalytic oxygen carriers and sustainable oxidative coupling of methane in chemical-looping scheme

Reversible Exsolution of Iron from Perovskites for Highly Selective Syngas Production Via Chemical Looping Dry Reforming of Methane

Polymetallic doping of Mn-based perovskite oxides for chemical looping dry reforming of methane

Alkali-metal enhanced LaMnO3 perovskite oxides for chemical looping oxidative dehydrogenation of ethane

Uniformly dispersed NiFeAlO 4 as oxygen carrier for chemical looping steam methane reforming to produce syngas

Mn-Fe-Al-O Mixed Spinel Oxides As Oxygen Carrier for Chemical Looping Hydrogen Production with CO2 Capture

LaFe0.8Co0.15Cu0.05O3 Supported on Silicalite-1 as a Durable Oxygen Carrier for Chemical Looping Reforming of CH4 Coupled with CO2 Reduction

Effect of Ba content on chemical looping dry reforming of methane performance of(La0.5Sr0.5)1-xBaxFe0.6Co0.4O3

Thermochemically Stable Novel Oxygen Carriers Based on CaMn1- x- y Ti x Fe y O3-δ for Chemical Looping

Co-production of syngas and H2 from chemical looping steam reforming of methane over anti-coking CeO2/La0.9Sr0.1Fe1−xNixO3 composite oxides

Enhanced performance of LaFeO3 oxygen carriers by NiO for chemical looping partial oxidation of methane

Enhanced oxygen migration in tailored lanthanum-based perovskite for solar-driven dry reforming of methane

Achieving surface and bulk rate matching for chemical looping partial oxidation of methane by modulating oxygen transport