<i>In-situ</i> TEM investigation of dislocation loop reaction and irradiation hardening in H₂<SUP>+</SUP>-He<SUP>+</SUP> dual-beam irradiated Mo

Yipeng Li,Guang Ran,Xinyi Liu,Qing Han,Xiuyin Huang,Yifan Ding

DOI: https://doi.org/10.1016/j.jmst.2021.07.040

2022-01-01

Abstract:Through in-situ TEM observation during 30 keV H-2(+)-He+ dual-beam irradiation at 723 K, the reaction and transformation of dislocation loops in pure Mo were investigated, especially for < 100 > loops. Irradiation could directly cause the formation of 1/2 < 111 > loops and < 100 > loops, but 1/2 < 111 > loops were dominant. In-situ observation confirmed the formation mechanism of < 100 > loops, including direct irradiation induced mechanism, 1/2 < 111 > loop direct conversion mechanism, and reaction mechanism of two 1/2 < 111 > loops. Meanwhile, the reaction of two 1/2 < 111 > loops to produce < 100 > loop should not require the strict size similarity condition. The reaction between 1/2 < 111 > loops could also produce 1/2 < 111 > loop, which was essentially a process in which one loop absorbed another one. The yield strength increment caused by irradiation-induced loops was analyzed, and its saturation value reached 0.48 GPa at 0.06 dpa. Compared with single He+ irradiation, the number density and average diameter of loops increased significantly and more serious damage was caused under the synergistic effect of hydrogen and helium. The mechanism based on in-situ experimental observation was discussed in depth. (C) 2022 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.