Abstract:In situ irradiations with 30 keV He+ have been performed on W–0.5 wt % ZrC at 823 and 1073 K. Detailed characterization showed that the dislocation loops around the ZrC particles with the size range of ∼120–370 nm were lower in density and smaller than that far away from these particles. The larger the sizes of ZrC particles, the lower the density and smaller the sizes of dislocation loops around the particles would be. In contrast, the higher density of dislocation loops with larger sizes around the ZrC particles with the size range of ∼20–60 nm was displayed. The interaction between a ⟨100⟩ dislocation line and a ⟨100⟩ dislocation loop was in situ observed and investigated by molecular dynamics simulation for the first time. The reacted ⟨100⟩ dislocations with the orthogonal Burgers vectors are more likely to be responsible for the interaction than that with the parallel geometry. The interaction required the generation of glissile 1/2⟨111⟩ dislocation segments, which acted as an "intermediate bridge" between the reacted sessile dislocations. The current results will be of benefit to deeply understand the irradiation behavior of the W–ZrC alloy acting as the plasma-facing materials for the application of fusion reactors.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c03915.SRIM profile of irradiation damage and injected helium concentration as a function of irradiation depth, g·b = 0 invisibility criterion close to [001] to determine the types of dislocation loops, and geometry for dislocation line l2 and dislocation loop n under two-beam diffraction conditions g = 110 and g = 11̅0 close to [001] (PDF)This article has not yet been cited by other publications.

Micron-scale 1D migration of interstitial-type dislocation loops in aluminum

The evolution of dislocation loop and its interaction with pre-existing dislocation in He+-irradiated molybdenum: in-situ TEM observation and molecular dynamics simulation

In Situ Transmission Electron Microscopy Study of Growth of Dislocation Loops in Fe-Ni Alloy under Ion Irradiation

In-situ TEM investigation of 30 keV he+ irradiated tungsten: Effects of temperature, fluence, and sample thickness on dislocation loop evolution

Formation of helical dislocations mediated by interstitials in ion irradiated FeCrAl alloy

Effect of ion flux on one-dimensional migration of dislocation loops in Fe9Cr1.5W0.4Si F/M steel during in-situ Fe + irradiation

In-situ TEM investigation of dislocation loop evolution in Al-forming austenitic stainless steels during Fe+ irradiation: Effects of irradiation dose and pre-existing dislocations

Evolution of dislocation loops in irradiated α-Uranium: An atomistically-informed cluster dynamics investigation

Comparison of the Time-Dependent Physical Processes in the Electromigration of Deep Submicron Copper and Aluminum Interconnects

Fundamental Insights into the Mass Transfer Via Full Dislocation Loops Due to Alternative Surface Cuts

New Mechanisms of Helical Dislocation Formation Via the Pinch-off Process Near a Nano-Inhomogeneity

Evolution of Dislocation Loops in 30 keV He + -Irradiated W–0.5% ZrC Alloys: In Situ TEM Observations and Molecular Dynamics Simulations

Dynamic observation of dual-beam irradiated Fe and Fe-10Cr alloys at 435 °C

Coupled effect of Cr and Al on interactions between a prismatic interstitial dislocation loop and an edge dislocation line in Fe-Cr-Al alloy

In-situ TEM analysis on early-stage evolution of dislocation loops in 30 keV H2+ irradiated W

TEM Investigation on the Dislocation Loops in Zirconium Alloy by Neutron and Kr+ Ion Irradiation Tests

Molecular dynamics study on the Burgers vector transition of nanometric dislocation loops induced by cascade in bcc-iron

Atomistic simulations of nano-fiber-confined metal plasticity

Effect of hydrogen, helium and dose rate on the evolution of dislocation loop in pure iron during in-situ irradiation

Atomistic Simulations for the Evolution of a U-shaped Dislocation in Fcc Al

Effect of Carbon on Dislocation Loops Formation during Self-Ion Irradiation in Fe-Cr Alloys at High Temperatures