Abstract:In situ irradiations with 30 keV He+ have been performed on W–0.5 wt % ZrC at 823 and 1073 K. Detailed characterization showed that the dislocation loops around the ZrC particles with the size range of ∼120–370 nm were lower in density and smaller than that far away from these particles. The larger the sizes of ZrC particles, the lower the density and smaller the sizes of dislocation loops around the particles would be. In contrast, the higher density of dislocation loops with larger sizes around the ZrC particles with the size range of ∼20–60 nm was displayed. The interaction between a ⟨100⟩ dislocation line and a ⟨100⟩ dislocation loop was in situ observed and investigated by molecular dynamics simulation for the first time. The reacted ⟨100⟩ dislocations with the orthogonal Burgers vectors are more likely to be responsible for the interaction than that with the parallel geometry. The interaction required the generation of glissile 1/2⟨111⟩ dislocation segments, which acted as an "intermediate bridge" between the reacted sessile dislocations. The current results will be of benefit to deeply understand the irradiation behavior of the W–ZrC alloy acting as the plasma-facing materials for the application of fusion reactors.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c03915.SRIM profile of irradiation damage and injected helium concentration as a function of irradiation depth, g·b = 0 invisibility criterion close to [001] to determine the types of dislocation loops, and geometry for dislocation line l2 and dislocation loop n under two-beam diffraction conditions g = 110 and g = 11̅0 close to [001] (PDF)This article has not yet been cited by other publications.

In-situ TEM analysis on early-stage evolution of dislocation loops in 30 keV H2+ irradiated W

In-situ TEM investigation of 30 keV he+ irradiated tungsten: Effects of temperature, fluence, and sample thickness on dislocation loop evolution

In-situ TEM observation and MD simulation of the reaction and transformation of loops in tungsten during H2+ & He+ dual-beam irradiation

The evolution of dislocation loop and its interaction with pre-existing dislocation in He+-irradiated molybdenum: in-situ TEM observation and molecular dynamics simulation

Evolution of Dislocation Loops in 30 keV He + -Irradiated W–0.5% ZrC Alloys: In Situ TEM Observations and Molecular Dynamics Simulations

Formation mechanism of 〈 111 〉 interstitial dislocation loops from irradiation-induced C15 clusters in tungsten

Phase-field simulation of dislocation interaction with damage loops created by irradiation in tungsten

Effect of dose rate on dislocation loop evolution in tungsten: Combination of defect generation rate and elastic interaction

Effect of different pre-existing dislocation densities on the microstructure evolution of W-0.5ZrC alloy during in-situ He+ irradiation

Molecular dynamics study on the Burgers vector transition of nanometric dislocation loops induced by cascade in bcc-iron

Dynamic observation of dual-beam irradiated Fe and Fe-10Cr alloys at 435 °C

Investigation of microstructural evolution of irradiation-induced defects in tungsten: an experimental-numerical approach

Influence of rhenium-decorated dislocation loops on edge dislocation gliding in tungsten

TEM Investigation on the Dislocation Loops in Zirconium Alloy by Neutron and Kr+ Ion Irradiation Tests

The Behaviors of Dislocation Loops Punched by Helium Interstitials Accumulation under the Temperature Gradient Field in Tungsten

Initial microstructure and temperature dependence of irradiation defects evolution in tungsten

Orientation dependence of shock-induced change of habit plane for the 1/2 dislocation loop and plasticity in tungsten

Hydrogen induced dislocation core reconstruction in bcc tungsten

An Atomistic Modelling Study of the Properties of Dislocation Loops in Zirconium

Effect of hydrogen, helium and dose rate on the evolution of dislocation loop in pure iron during in-situ irradiation

Formation of < 100 > Vacancy Dislocation Loops from Two-Dimensional Vacancy Platelets in Body-Centered Cubic Iron