Effect of Hydrogen on Microstructure Evolution and Deformation Behaviors of Ti-2Fe-0.1B Alloy

Biao Zhang,Yuyang Wang,Hui Chang,I. Alexandrov,Zhonggang Sun,Yuecheng Dong,R. Z. Valiev,Yaoqi Wang,Lian Zhou
DOI: https://doi.org/10.1016/j.jallcom.2021.163473
IF: 6.2
2021-01-01
Journal of Alloys and Compounds
Abstract:A low-cost Ti-2Fe-0.1B alloy with high performance was manufactured and hydrogenated in this study. The effect of 0.3 wt% hydrogen addition on microstructure evolution, compression deformation behavior at room and high temperature of Ti-2Fe-0.1B alloy has been investigated. Results indicated that lamellar alpha(L) structure along with martensite a' are formed after hydrogenation compared with initial equiaxed grains, and the fraction of beta phase increased from 4.95% to 30.1%. Obvious phase transformation alpha(eq)->alpha(H) + beta(H), beta -> H during hydrogenation and beta(H)->alpha + delta, alpha(H)->alpha + delta during subsequent cooling occurred. The hydrogenated Ti-2Fe-0.1B alloy is characterized by hardening effect during compression deformation at room temperature along with the loss of ductility due to the solid solution strengthening by hydrogen atoms and presence of hydride delta. However, peak flow stress of hydrogenated Ti-2Fe-0.1B alloy decreased from 49 MPa to 29 MPa extremely during compression deformation at 973 K, which can be attributed to the high volume of beta phase induced by hydrogenation, as well as the promotion of dynamic recovery and dynamic recrystallization. (C) 2021 Elsevier B.V. All rights reserved.
What problem does this paper attempt to address?