Abstract:Conventional rolled Mg-Al alloy sheets typically exhibit strong basal textures that remain and may even strengthen after recrystallization annealing due to the preferential growth of basal-oriented grains, resulting in poor formability at room temperature. Therefore, the knowledge of recrystallization and grain growth is critical for modifying textures of Mg-Al alloy sheets. The static recrystallization and texture evolution in a cold-rolled dilute Mg-1Al (wt.%) alloy during various annealed temperatures ranging from 300 °C to 450 °C, have been investigated using the quasi in-situ electron backscatter diffraction (EBSD) method. The as-rolled Mg-1Al alloy shows a dominant basal texture, which weakens and broadens in the rolling direction (RD) during the subsequent annealing, accompanied by the formation of 〈101¯0〉 texture component. Particularly, the 〈101¯0〉 texture component is more pronounced after annealing at high temperatures. The quasi in-situ EBSD results show that recrystallized grains are mainly induced by shear bands, which exhibit a wide spectrum of orientations with c-axis tilt angles ranging 20°-45° from the normal direction (ND). Orientations of shear band-induced recrystallized grains are retained during the entire recrystallization process, resulting in a reduction in the texture intensity. Moreover, recrystallized grains belonging to the 〈101¯0〉 texture component grow preferentially compared to those with other orientations, which is attributed to low energy grain boundaries, especially grain boundaries with ∼30° misorientation angles. Furthermore, the high temperature annealing facilitates the rapid growth of grain boundaries having a 30° misorientation angle, leading to the occurrence of distinct 〈101¯0〉 texture after annealing at 450 °C for 1 h. The results provide insights for texture modification of rare earth-free low-alloyed Mg alloys by controlling annealing parameters.

Texture Evolution of Hot Rolled Al–Cu–Mg–Zr Alloy During Annealing

Effect of S Phase Characteristics on the Formation of Recrystallization Textures of an Al-Cu-Mg Alloy

Coincidence Site Lattice Boundary Mechanism for the Preferred Growth of Goss and Cube Grains During Annealing in an Al-Cu-Mg Alloy

Enhanced Brass texture of hot-rolled Al-4Cu-1.6Mg alloy by 0.1% Zr addition

Micro-mechanism of Texture Evolution During Isochronal Annealing of As-Annealed Hot Rolled Al-Cu-Mg Sheet

Formation and development of Goss texture in Al–Cu–Mg alloy during solution treatment

New insight of texture and microstructure evolution, and the connections between with tensile performance in as-annealed Al-Cu-Mg-Zr sheet

Evolution of the Brass Texture in an Al-Cu-Mg Alloy During Hot Rolling

Microstructure and properties of Al-4.8Cu-0.45Mn-0.19Cd-0.18Ti-0.17Zr-0.14V aluminum alloy extrusion bar

Evolution of Goss Texture in an Al–Cu–Mg Alloy During Cold Rolling

Evolution of Texture, Microstructure, Tensile Strength and Corrosion Properties of Annealed Al–Mg–Sc–Zr Alloys

Development of A Strong Goss Texture During Annealing of A Heavily Rolled Al-0.3% Cu Alloy

Texture Evolution in an Al-Cu-Mg Alloy During Hot Rolling

Evolution of Microstructure, Texture, and Hardness in an Al-Cu-Mg Alloy During Annealing

Unexpected texture transition induced by grain growth during static annealing of a dilute Mg-1Al alloy

Microstructure and Texture Evolution in the Cryorolled CuZr Alloy

Development of Goss Texture in Al–0.3%Cu Annealed after Heavy Rolling

Evolution of Microstructures and Textures of High Purity Aluminium During Rolling and Annealing

The Preferential Growth and Related Textural Evolution During Static Recrystallization in a Cold-Rolled Mg–Zn–Gd Alloy

Evolution of texture and microstructure of 2E12 aluminum alloy during cold rolling and annealing

Insights into the evolution of texture and mechanical properties during warm rolling and annealing of Mg–2Zn-0.5Ca alloy