Abstract:Fe–Ni–Co–Al-based systems have attracted a lot of interest due to their large recoverable strain. In this study, the microstructure and thermal cycling behaviors of Fe41Ni28Co17Al11.5Ti1.25Nb1.25 (at.%) 98.5% cold-rolled alloys after annealing treatment at 1277 °C for 1 h, followed by aging for 48 h at 600 °C, were investigated. From the electron backscatter diffraction results, we see that the texture intensity increased from 9.4 to 16.5 mud and the average grain size increased from 300 to 400 μm as the annealing time increased from 0.5 h to 1 h. The hardness results for different aging heat treatment conditions show the maximum value was reached for samples aged at 600 °C for 48 h (peak aging condition). The orientation distribution functions (ODFs) displayed by Goss, brass, and copper were the main textural features in the FeNiCoAlTiNb cold-rolled alloy. After annealing, strong Goss and brass textures were formed. The transmission electron microscopy (TEM) results show that the precipitate size was ~10 nm. The X-ray diffraction (XRD) results show a strong peak in the (111) and (200) planes of the austenite (⁠⁠γ, FCC) structure for the annealed sample. After aging, a new peak in the (111) plane of the precipitate (⁠⁠γ′, L12) structure emerged, and the peak intensity of austenite (⁠⁠γ, FCC) decreased. The magnetization–temperature curves of the aged sample show that both the magnetization and transformation temperature increased with the increasing magnetic fields. The shape memory properties show a fully recoverable strain of up to 2% at 400 MPa stress produced in the three-point bending test. However, the experimental recoverable strain values were lower than the theoretical values, possibly due to the fact that the volume fraction of the low-angle grain boundary (LABs) was small compared to the reported values (60%), and it was insufficient to suppress the beta phases. The beta phases made the grain boundaries brittle and deteriorated the ductility. On the fracture surface of samples after the three-point bending test, the fracture spread along the grain boundary, and the cross-section microstructural results show that the faces of the grain boundary were smooth, indicating that the grain boundary was brittle with an intergranular fracture.

Occurrence of the R-phase with Increased Stability Induced by Low Temperature Precipitate-Free Aging in a Ni50.9Ti49.1 Alloy

Structural Evolution of Topologically Closed Packed Phase in a Ni-based Single Crystal Superalloy

The Effects of Ti3Ni4 Precipitates on the R-phase Transformation

Precipitation and Coarsening Kinetics of H-phase in NiTiHf High Temperature Shape Memory Alloy

An in Situ TEM Study of the Size Effect on the Thermally Induced Martensitic Transformation in Nanoscale NiTi Shape Memory Alloy

R-Phase Transformation Evolution in NiTi SMA Wires Studied via the Internal Friction Technique

Structure, Martensitic Transformations, and Mechanical Properties of Aging Nanocrystalline Ti–50.9 at % Ni Alloy

Abnormal superelastic cyclic behavior and stress-induced martensitic transformation mechanism of NiTi alloy with R phase

Effect of ageing treatment on the transformation behaviour of Ti-50.9 at.% Ni alloy

The Role of H-phase in Thermal Hysteresis and Shape Memory Properties in Ni50Ti30Hf20alloy

The role of the ω phase on the microstructure evolution of precipitation and mechanical property in Ti-3Al-5Mo-4Cr-2Zr-1Fe

In-Situ High-Energy Synchrotron X-Ray Diffraction Study of Micromechanical Behavior of Multiple Phases in Ni47ti44nb9 Shape Memory Alloy

P phase precipitation and strengthening behavior of a novel polycrystalline Ni 3 Al-based intermetallic alloy at 1100 °C

In Situ Synchrotron Radiation X-ray Diffraction Study on Phase and Oxide Growth during a High Temperature Cycle of a NiTi-20 at.% Zr High Temperature Shape Memory Alloy

In-situ synchrotron high energy X-ray diffraction study of micro-mechanical behaviour of R phase reorientation in nanocrystalline NiTi alloy

Investigation of the Ageing-Induced R-phase and Its Impact on Static/cyclic Tensile Failure in Ni50.9Ti49.1 Wire

Comparative study of physical properties of shape memory alloys after solution treating and aging at

Microstructural Evolution in NiTi Alloy Subjected to Surface Mechanical Attrition Treatment and Mechanism

Thermal Cycling Behavior of Aged FeNiCoAlTiNb Cold-Rolled Shape Memory Alloys

The influence of dislocations on R-phase transformations in a NiTi shape memory alloy

Effect of Aging on Martensitic Transformation and Superelasticity of TiNiCr Shape Memory Alloy