Interface characterization and mechanical properties of Mo-added chromium carbide-nickel composite
Liang Sun,Weihua Hui,Liujie Xu,Wenyan Zhai,Hui Dong,Yiran Wang,Lin He,Jianhong Peng
DOI: https://doi.org/10.1016/j.ceramint.2020.07.184
IF: 5.532
2020-12-01
Ceramics International
Abstract:<p>A novel chromium carbide–nickel composite was <em>in situ</em> fabricated through pressureless sintering in a vacuum furnace using Cr, C, Ni and Mo mixed powders. In this study, the Mo content distribution on interface characterization including the effect of phase transformation mechanism and mechanical properties of the composite were researched thoroughly. The results indicated that a newly found and excellent semi-coherent boundary existed between Cr<sub>3</sub>C<sub>2</sub> and Ni, which was (002)<sub>Cr3C2</sub>//(11<span class="math"><math>1(_)</math></span>)<sub>Ni</sub>, [1<span class="math"><math>2(_)</math></span>0]<sub>Cr3C2</sub>//[011]<sub>Ni</sub>. Their disregistry along the particular orientation relationship was approximately 10.6%, indicating that Cr<sub>3</sub>C<sub>2</sub> could serve as an efficient heterogeneous nucleation area of Ni. An interdiffusion and phase transformation occurred in the microstructure, Mo element tended to solid solute into the carbide matrix which changed from (Cr, Ni)<sub>3</sub>C<sub>2</sub> to (Cr, Mo)<sub>3</sub>C<sub>2</sub>, and (Cr, Mo, Ni)<sub>7</sub>C<sub>3</sub>. Moreover, according to DFT calculation for contain phases as well as the Rockwell hardness, bending strength, and fracture roughness were enhanced simultaneously, it was attributed to grain refinement, solution strengthening, and better mechanical properties of the (Cr, Mo, Ni)<sub>7</sub>C<sub>3</sub> phase.</p>
materials science, ceramics