Anti-ablation performance of plasma sprayed ZrB 2 /SiC coatings on C/C substrates and the influence of a chemical vapor deposited SiC interlayer
Zhi-ting Gao,Zhuang Ma,Qiang Liu,Ze Zhang,Yi-fan Wang,Shao-pu Liu,Ling Liu,Yan-bo Liu
DOI: https://doi.org/10.1016/j.mtcomm.2023.106591
IF: 3.8
2023-07-14
Materials Today Communications
Abstract:To address the industrial usage of carbon/carbon (C/C) substrates with plasma-sprayed ZrB 2 /SiC coatings, a continuous and dense chemical vapor deposition (CVD)-SiC interlayer of 150 μm was deposited on a C/C substrate. The integration of CVD-SiC with the C/C substrate and plasma sprayed (PS) ZrB 2 /SiC coatings results in a tight interface. The SiC interlayer significantly reducing thermal stress in the optimized composites up to 1828 Mpa, a decrease of approximately 60% compared to standard composites without CVD-SiC. Ablation tests conducted showed that the optimized composite displayed remarkable mass ablation rate of − 11.7% after ablation for 600 s, with a notable increase of − 3.5% even after ablation for 1800 s. After 600 s of ablation, the exposed SiO 2 layer is approximately 500 μm in size. After 900 s of ablation, the exposed SiO 2 layer is approximately 1500 μm. After 1800 s of ablation, the SiO 2 is completely evaporated, exposing the C/C matrix, at which point the coating has failed. The SiC interlayer improve the ablation resistance due to the continuous SiO 2 film formed by the self-sealing and O anti-diffusive properties.
materials science, multidisciplinary