Abstract:To improve the ablation resistance of C/C composites, ZrB2-SiC composite coatings were deposited on C/C composites by atmospheric plasma spraying (APS) process. Ablation tests were carried out on the ZrB2-SiC coated C/C composites using Oxygen-propane torch. The microstructures and phases of the coatings were analyzed by XRD, SEM and EDS. The results show that uniform and dense ZrB2-SiC composite coatings can be fabricated on the C/C composites by atmospheric plasma spraying (APS). After ablation at 1 600, 1 700 and 1 800 °C for 300 s, the weight of ZrB2-SiC coated C/C composites increases by 0.63%, 0.76% and 0.71%, respectively. While after ablation at 1 600, 1 700 and 1 800 °C for 600 s, the mass ablative rate of the coated specimen is 9.42×10, 2.04×10 and 1.04×10 g/s, respectively. The ZrB2-SiC composite coatings effectively enhance the ablation-resistance of C/C composites, and the oxidation product SiO2 can fill in the pores in the coatings. However, after the exhaustion of SiO2, the pores in the coating became the channels of the oxygen diffused into the C/C substrate, resulting in the failure of C/C substrate.

Ablation Behavior of Zrc-La2o3 Coating for Sic-Coated Carbon/Carbon Composites under an Oxyacetylene Torch

Ablation behavior of rare earth La-modified ZrC coating for SiC-coated carbon/carbon composites under an oxyacetylene torch

Ablation Behaviors and Mechanism of ZrC-SiC-Si/SiC-Si Double-Layered Coatings on C/C Composite under Plasma Flame at 3000 °C

Ablation Behavior of ZrB 2 -Based Coating Prepared by Supersonic Plasma Spraying for SiC-Coated C/C Composites under Oxyacetylene Torch

Anti-ablation Performance of La2O3-modified ZrB2 Coating on SiC-coated Carbon/carbon Composites

Microstructures and Ablation Resistance of Zrc Coating for Sic-Coated Carbon/Carbon Composites Prepared by Supersonic Plasma Spraying

Ablation Behavior of ZrC and ZrO2 Coatings on SiC Coated C/C Composites under Oxyacetylene Torch with Different Heat Fluxes

Ablation Resistance of ZrB2–SiC Coating Prepared by Supersonic Atmosphere Plasma Spraying for SiC-coated Carbon/carbon Composites

Ablation Behavior of Single and Alternate Multilayered ZrC-SiC Coatings under Oxyacetylene Torch

Effect of Monolithic LaB 6 on the Ablation Resistance of ZrC/SiC Coating Prepared by Supersonic Plasma Spraying for C/C Composites

A Multilayer SiC/ZrB2/SiC Ablation Resistance Coating for Carbon/Carbon Composites

SiC/ZrB2–SiC–ZrC Multilayer Coating for Carbon/carbon Composites Against Ablation

Ablation resistance of supersonic-atmosphere-plasma-spraying ZrC coating doped with ZrO2 for SiC-coated carbon/carbon composites

Ablation Behavior under Oxyacetylene Torch of ZrC Coating Modified by SiC/TaC Nanocomposites

Ablation Resistance of Different Coating Structures for C/ZrB2–SiC Composites under Oxyacetylene Torch Flame

Preparation and ablation properties of ZrC-SiC coating for carbon/carbon composites by solid phase infiltration

Ablation-resistance of ZrB2-SiC Coating under Oxygen-propane Torch Flame Prepared by Atmospheric Plasma Spraying

Ablation resistance and mechanism of SiC/ZrC-ZrB2 double layer coating for C/C composites under plasma flame

Ablation Mechanism and Properties of SiO2 Modified ZrB2-SiC Coatings Fabricated on C/C Composites Via Plasma Spraying Technology

Ablation Resistance of SiC–ZrC Coating Prepared by a Simple Two-Step Method on Carbon Fiber Reinforced Composites

Microstructure and Ablation Mechanism of SiC-ZrC-Al2O3 Coating for SiC Coated C/C Composites under Oxyacetylene Torch Test