Experimental and Dft Studies on Diesel-Steam-Reforming to Hydrogen over a Bimetallic Rh–Ni Microsphere Catalyst

Qiangqiang Xue,Huilin Yi,Zhengwen Li,Zhao Jiang,Meng Chen,Yujun Wang,Binhang Yan,Guangsheng Luo

DOI: https://doi.org/10.2139/ssrn.3978743

2021-01-01

Abstract:Surface modification of 600-µm-sized monodisperse gamma-alumina microspheres into magnesium-aluminum spinel, and co-impregnation-based loading of Rh–Ni were performed to synthesize catalysts for diesel-steam-reforming to hydrogen. The intimate interactions between Rh and Ni, the formation of the Rh–Ni alloy, and the Rh-doping-induced decrease in the particle size of Ni were determined. The DFT calculations results revealed that Rh-doped Ni(111) established remarkably weak bonds with oxygen-containing intermediates, and the reaction barrier of the rate-limiting step (CH2* + O*→ CH2O*) on Rh–Ni(111) (0.76 eV) was lower than those of Ni(111) (1.14 eV) and Rh(111) (1.56 eV). The bimetallic catalyst shows the enhanced activity and resistance of sintering and carbon deposition compared with those of Ni-based and Rh-based catalysts. The catalytic performance of Rh–Ni-based catalyst was superior to that of physically mixed Ni-based and Rh-based catalysts at similar active metal loadings, which further confirmed the synergistic effect of Rh–Ni.