A Study on the Corrosion Behavior of RGO/Cu/Fe-Based Amorphous Composite Coatings in High-Temperature Seawater

Zhenhua Chu,Yunzheng Zhang,Wan Tang,Yuchen Xu,Jingxiang Xu
DOI: https://doi.org/10.3390/coatings14050556
IF: 3.236
2024-05-01
Coatings
Abstract:In this paper, based on an Fe-based amorphous alloy, four kinds of RGO/Cu/Fe-based amorphous composite coatings with mass ratios of 5%, 10%, 15%, and 20% of RGO/Cu were prepared on the surface of 45# steel by using high-velocity oxy-fuel (HVOF) spraying. The coatings were immersed in simulated seawater at room temperature and at 90 °C for different lengths of time, and their corrosion resistance was tested using electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM), and X-ray diffraction (XRD), and the surface morphology and phase distribution of the samples were observed. The results showed that with the increase in the introduction ratio of RGO/Cu, when the addition ratio reached 15%, the composite coating had the best corrosion resistance. After soaking in simulated seawater at 90 °C for 18 days, the surface of the coating showed slight peeling and crack propagation, but no obvious pitting phenomenon occurred. The corrosion mechanism of the RGO/Cu/Fe coating in high-temperature seawater is mainly that high temperature causes the cracking of the coating, which opens up a transport channel for corrosion media. However, due to the addition of RGO, the corrosion has a certain self-limitation effect, which is mainly due to the toughening effect of RGO on the coating and its effect on extending the corrosion channel.
materials science, multidisciplinary, coatings & films,physics, applied
What problem does this paper attempt to address?
### Problems the Paper Attempts to Solve The paper primarily investigates the corrosion behavior of RGO/Cu/Fe-based amorphous composite coatings in high-temperature seawater environments. Specifically, the paper attempts to address the following issues: 1. **Improving the Corrosion Resistance of Marine Engineering Equipment**: As terrestrial resources become increasingly depleted, attention has turned to the development of marine resources. However, marine equipment (such as ships and offshore platforms) operating in seawater environments containing moist salt are subject to severe corrosion. Traditional metal materials offer limited protection in such harsh marine environments. 2. **Studying the Corrosion Performance of RGO/Cu Composite Coatings in Different Proportions**: Four different mass ratios (5%, 10%, 15%, 20%) of RGO/Cu/Fe-based amorphous composite coatings were prepared using plasma spraying technology. Immersion experiments of varying durations were conducted in simulated seawater to test their corrosion resistance. 3. **Evaluating the Optimal RGO/Cu Addition Ratio**: Using methods such as Electrochemical Impedance Spectroscopy (EIS), Scanning Electron Microscopy (SEM), and X-ray Diffraction (XRD), it was determined that when the mass ratio of RGO/Cu reaches 15%, the composite coating exhibits the best corrosion resistance. 4. **Exploring the Mechanism of High-Temperature Seawater on the Coating**: The study found that after 18 days of immersion in 90°C seawater, the coating surface showed slight peeling and crack propagation, but no significant pitting corrosion occurred. High temperatures caused the coating to crack, forming channels for the transmission of corrosive media. However, due to the addition of RGO, there was a certain self-limiting effect on corrosion, mainly due to the toughening effect of RGO on the coating and its role in extending the corrosion channels. In summary, the paper aims to improve the corrosion resistance of RGO/Cu/Fe-based amorphous composite coatings in high-temperature seawater environments by optimizing their formulation, thereby providing better protection for marine engineering equipment.