Abstract:Generally, elevated nitrogen (N) content promotes the precipitation of nitrides, which increase the size and quantity of porosity and thus degrade the mechanical performance of superalloys. However, in this study, N content was found to have a beneficial impact on the stress rupture property of single-crystal (SX) superalloys. The results indicated that as the N content increased from 5 ppm to 35 ppm, the porosity first decreased and then increased. The porosity of the sample with 14 ppm N was the lowest, 0.072% ± 0.011%, which was mainly attributed to the TiN phases in interdendritic pools that compensated for volume shrinkage by lattice expansion. The addition of N reduced the volume fraction and antiphase boundary energy of the γ′ phase because TiN nitride formation consumed Ti in large quantities. Additionally, the rupture life at 1100 °C/130 MPa was abnormally improved to 251.67 h ± 19 h as the N content was increased to 14 ppm, while it was markedly decreased as the N content was continuously increased to 35 ppm. The improved stress fracture life of the alloy was primarily attributed to the formation of TiN with a small size, which retarded microporosity formation and effectively impeded dislocation movement in γ channels. Moreover, during the stress rupture test, the size of the tertiary γ′ phase first reduced to a minimum in the alloy containing 14 ppm N, which increased the resistance to dislocation movement. However, excessive addition of N drastically reduced the stress fracture life as the precipitation and solid solution strengthening in the γ′ phase weakened. In addition, the agglomeration of nitride inclusions formed defects that aggravated crack nucleation and propagation. The overall N impact was studied, and the optimal N content was ascertained to provide further instructions for the commercial development of Re-free second-generation SX alloys.

Stress induced anisotropic diffusion during plasma-aided nitriding of a Ni-based superalloy

Effect of Substrate Characteristics on Interdiffusion Coefficients of Ni and Al Atoms in Β-Nial Phase of Aluminide Coatings

Evolution of residual stress in the diffusion zone of a model Fe-Cr-C alloy during nitriding*

The Effect of Stress Gradient on the Formation of TCP Phases in a Ni-based Single Crystal Superalloy at 1050 Oc

Stress-induced influence on the evolution of γ′ phase in dendritic area during long-term stress aging at 900 °C in Ni-based superalloy K444

Modeling of Oxygen Diffusion Along Grain Boundaries in a Nickel-Based Superalloy

The Dependence of Stress and Strain Rate on the Deformation Behavior of a Ni‐based Single Crystal Superalloy at 1050°C

Influences of stress-aging on the precipitation behavior of δ phase (Ni3Nb) in a nickel-based superalloy

The Effect of Ni Plating on the Residual Stress and Micro-Yield Strength in an Al-Cu-Mg Alloy Under Different Diffusion Treatments

Laser assisted nitriding of nickel–chromium-based superalloy surface: Heating and diffusion analysis

A Study of the Internal Deformation Fields and the Related Microstructure Evolution during Thermal Fatigue Tests of a Single-Crystal Ni-Base Superalloy

An investigation on nitrogen uptake and microstructure of equimolar quaternary FeCoNiCr high entropy alloy after active-screen plasma nitriding

Evolution of residual stress and its impact on Ni-based superalloy

Effect of heat treatment on the microstructural evolution of a nickel-based superalloy additive-manufactured by laser powder bed fusion

Effects of Stress State, Crack—γ/γ′ Phase Interface Relative Locations and Orientations on the Deformation and Crack Propagation Behaviors of the Ni-Based Superalloy—A Molecular Dynamics Study

Stress Concentration Induced by the Crystal Orientation in the Transient-Liquid-Phase Bonded Joint of Single-Crystalline Ni3Al

Study of the influence of shape, orientation, and size of AlN in the γ′-free zone of nickel-based superalloys by microstructure-based numerical models

Stress-assisted Atomic Diffusion in NiTiHf Shape Memory Alloys

On the Residual Stress Relaxation in Inconel 718 Superalloys at High Temperature by Real-Time Neutron Diffraction

Abnormal improvement of high-temperature stress rupture life in a new low cost Ni-based single crystal superalloy by adding minor nitrogen

X-ray Residual Stress Analysis of Nitrided Low Alloyed Steels