Abstract:Longitudinal crack defects are a frequent occurrence on the surface of thin slabs during the high-speed continuous casting process. Therefore, this study undertakes a detailed analysis of the solidification characteristics of hyper-peritectic steel thin slabs. By establishing a three-dimensional heat transfer numerical model of the thin slab, the formation mechanism of longitudinal cracks caused by uneven growth of the initial shell is determined. Based on the mechanism of longitudinal crack formation, by adjusting the performance parameters of the mold flux, the contradiction between the heat transfer control and lubrication improvement of the mold flux is fully coordinated, further reducing the incidence of longitudinal cracks on the surface of the casting thin slab. The results show that, using the optimized mold flux, the basicity increases from 1.60 to 1.68, the F- mass fraction increases from 10.67% to 11.22%, the Na2O mass fraction increases from 4.35% to 5.28%, the Li2O mass fraction increases from 0.68% to 0.75%, and the carbon mass fraction reduces from 10.86% to 10.47%. The crystallization performance and rheological properties of the mold flux significantly improve, reducing the heat transfer performance while ensuring the lubrication ability of the molten slag. After optimizing the mold flux, a surface detection system was used to statistically analyze the longitudinal cracks on the surface of the casting thin slab. The proportion of longitudinal cracks (crack length/steel coil length, where each coil produced is about 32 m long) on the surface of the thin slab decreases from 0.056% to 0.031%, and the surface quality of the thin slab significantly improves.

Research on Defects of 09Cupcrni-a of Beam Blank Continuous Casting

Beam Blank Continuous Casting Technology and Its Research

Numerical Simulation of the Thermo-Mechanical Process for Beam Blank Continuous Casting

Thermomechanical Analysis and Optimisation for Beam Blank Continuous Casting

Thermo-mechanical simulation and parameters optimization for beam blank continuous casting

Analysis and control of surface cracks in a B-bearing continuous casting blooms

A review of research on central crack in continuous casting strand

Laser Cladding Fe/FeCr Coatings on Continuous Casting Cu Mold

Analysis of Longitudinal Cracking and Mold Flux Optimization in High-Speed Continuous Casting of Hyper-Peritectic Steel Thin Slabs

Prevention of transverse corner crack in continuous casting slab by adjusting cooling schedule

Three-Dimensional Fem Study of Fluid Flow in Mould for Beam Blank Continuous Casting: Influence of Straight Through Conduit Type Sen

Analysis and Improvement of H-beam for Offshore Oil Platform Production Process

Formation and control of the surface defect in hypo-peritectic steel during continuous casting: A review

Steel Edge Cracking Analysis and Improvement Measures

Analysis of the Formation Mechanism of Surface Cracks of Continuous Casting Slabs Caused by Mold Wear

The Effect of Temperature, Cooling Rate and Casting Speed on Quality of Continuous Cast Steel Billets

Improving the casting process of peritectic steel grades

Research on the formation mechanism and fracture behavior of bifilm defects

Analysis of Internal Cracks in High Carbon Casting Bloom Induced by Soft Reduction Process and Its Improvement Using Numerical Simulations and Industrial Experiments

Research Status of High-Manganese High-Aluminum Steel and Key Points of Continuous Casting

Effects of Surface Defects on Rolling Contact Fatigue in 10Cr4ni4mo4v