Synthesis of Na2Mn0.8Fe0.2Fe(CN)6 and Its Application As Cathode Material of Sodium Ion Battery

Zhao Liu,Wei Zhang,Yan Jiang
DOI: https://doi.org/10.1088/1755-1315/621/1/012061
2021-01-01
IOP Conference Series Earth and Environmental Science
Abstract:The Prussian blue cathode material with a unique three-dimensional structure in sodium ion batteries had great potential. Na2MnFe(CN)(6) and Na2Mn0.8Fe0.2Fe(CN)(6 )cathode materials were prepared by the improved co-precipitation method of chelating agent, and the electrochemistry of the half-cell was tested. The results showed that the first discharge capacity of the two materials can reached 152.4mAh/g and 119.5mAh/g respectively at 0.1C(1C=170mA/g). The capacity retention rate of Na2MnFe(CN)(6) was only 43.2% after 100 cycles at 0.2C current density, but Na2Mn0.8Fe0.2Fe(CN)(6) can reached 70%. The capacity retention of Na2Mn0.8Fe0.2Fe(CN)(6) can still reached 69.8% after 100 cycles at 0.5C current density. The discharge specific capacity fluctuation of Na2Mn0.8Fe0.2Fe(CN)(6) was smaller than that of Na2MnFe(CN)(6).
What problem does this paper attempt to address?