Novel K+-doped Na0.6Mn0.35Fe0.35Co0.3O2 cathode materials for sodium-ion batteries: synthesis, structures, and electrochemical properties

Serap Gençtürk Tosun,Davut Uzun,Serkan Yeşilot
DOI: https://doi.org/10.1007/s10008-021-04906-0
IF: 2.747
2021-01-24
Journal of Solid State Electrochemistry
Abstract:A series of novel K<sub>x</sub>Na<sub>0.6-x</sub>Mn<sub>0.35</sub>Fe<sub>0.35</sub>Co<sub>0.3</sub>O<sub>2</sub> (<i>x</i> = 0, 0.005, 0.01, 0.05, 0.1) materials were successfully synthesized by the solid-state reaction method. The newly prepared cathode materials were examined by means of X-ray diffraction. They were characterized by scanning electron microscopy (SEM-EDS) and inductively coupled plasma mass spectrometry (ICP-OES). Their electrochemical performances for sodium-ion batteries were tested. The effects of varying K<sup>+</sup> doping content on the electrochemical battery performance on the prepared cathode materials were investigated. It was found that the potassium-doped K<sub>0.01</sub>Na<sub>0.59</sub>Mn<sub>0.35</sub>Fe<sub>0.35</sub>Co<sub>0.3</sub>O<sub>2</sub> showed the best electrochemical performance with an initial discharge capacity of 138.0 mAh g<sup>−1</sup> among them. The capacity retention after 20 cycles for Na<sub>0.6</sub>Mn<sub>0.35</sub>Fe<sub>0.35</sub>Co<sub>0.3</sub>O<sub>2</sub> (without K<sup>+</sup> doping) was 87.6%. After the potassium doped, the capacity retentions for K<sub>0.01</sub>Na<sub>0.59</sub>Mn<sub>0.35</sub>Fe<sub>0.35</sub>Co<sub>0.3</sub>O<sub>2</sub> and K<sub>0.005</sub>Na<sub>0.595</sub>Mn<sub>0.35</sub>Fe<sub>0.35</sub>Co<sub>0.3</sub>O<sub>2</sub> compounds were 90.8% and 90.6% respectively. These results proved that the appropriate amount of K<sup>+</sup> doping could be a feasible strategy to increase the cycling stability performance of layered cathode for sodium-ion battery.
electrochemistry
What problem does this paper attempt to address?