Cubic MnS–FeS 2 Composites Derived from a Prussian Blue Analogue as Anode Materials for Sodium-Ion Batteries with Long-Term Cycle Stability

Qian Liu,Shao-Jian Zhang,Cheng-Cheng Xiang,Chen-Xu Luo,Peng-Fang Zhang,Chen-Guang Shi,Yao Zhou,Jun-Tao Li,Ling Huang,Shi-Gang Sun

DOI: https://doi.org/10.1021/acsami.0c10874

2020-09-02

Abstract:Cubic N,S codoped carbon coating MnS–FeS₂ composites (MnS–FeS₂@NSC) with a hollow structure were prepared and used as anode materials for sodium-ion batteries. MnS–FeS₂@NSC exhibits excellent cycle performance and high rate capability and delivered a reversible capacity of 501.0 mAh g^–1 after 800 cycles at a current density of 0.1 A g^–1 with a capacity retention of 81%. More importantly, the MnS–FeS₂@NSC anode holds long-term cycle stability; the capacity can remain 134.0 mAh g^–1 after 14 500 cycles at 4 A g^–1. Kinetic analysis demonstrated that Na⁺ storage follows a pseudocapacitive dominating process, which is ascribed to the origin of the outstanding rate performance of the MnS–FeS₂@NSC material. The enhancement of electrochemical performance is attributed to the hollow structure and the N,S codoped carbon coating structure, which can reduce the diffusion distance for sodium ions and electrons, alleviate volume expansion during sodium-ion insertion/extraction, and retain the structural integrity effectively. Furthermore, a two-step sodiation processes with FeS₂ sodiation prior to MnS was demonstrated by X-ray diffraction (XRD), and the electrochemical impedance spectroscopy (EIS) spectra might indicate that the accumulation of the metallic elements in the preconversion reaction can accelerate the transfer of electrons and ions in the further conversion process.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c10874?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c10874</a>.Details for material synthesis, characterization, and electrochemical tests; XRD pattern of Mn[Fe(CN)₆]_0.67·<i>n</i>H₂O; EDS spectra and atomic percentage of MnS–FeS₂@NSC; SEM image of precalcined Mn–Fe–PBA in air; XRD pattern of MnS–FeS₂; <i>Z</i>_re–ω^–1/2 fitting curves of MnS–FeS₂@NSC and MnS–FeS₂; plots of ν^1/2 used for calculating constants <i>k</i>₁ and <i>k</i>₂ at different potentials; and capacitive and diffusion-controlled charge storage (MnS–FeS₂@NSC) contributions at different scan rates (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c10874/suppl_file/am0c10874_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology