Abstract:Cross-linked polyethylene(XLPE) insulating materials are widely used in the medium and high voltage cables because of their excellent electrical performances, as well as stable physical and chemical properties. With the long-term running of the XLPE cables, some degradation reactions of the insulating materials will happen under the action of long time thermal stress, which cause the irreversible changes for the chemical structure and morphology of these types insulating materials. The aging degradation will weaken the electrical properties of the cables and lead to insulation failure gradually, which brings about irreparable damage to the society and people. In this paper, both the resisting water tree and ordinary XLPE cable materials were selected as the study object, the aging temperature were set at 110°C, 130°C, 150°C to conduct accelerated aging experiments on the resisting water tree and ordinary XLPE cable materials, respectively. The effects of thermal aging on mechanical properties and electrical resistance of these XLPE insulation materials were studied, including the infrared transmission spectroscopy, the gel content, the tensile strength test and AC breakdown strength test and so on. The experimental results show that the tensile strength of the studied insulation materials increased firstly and then decreased at the selected aging temperatures. From 0 to 500 h of the aging time, the tensile strength of the two materials had a rising trend. The higher the aging temperature, the shorter the time to the turning point of the tensile strength. With the aging time prolonging, the tensile strength of both materials both decreased. And the tensile strength of the anti-water tree XLPE material was higher than that of ordinary XLPE. There exited significantly different with the absorption peak for both type XLPE materials in the 1000 cm -1 , which was due to the introduction of new functional groups to XLPE by the anti-water tree additive. As the aging temperature increased and the aging time was prolonged, the aging degree of ordinary XLPE materials was more severe than that of the antiwater tree XLPE insulation materials. The gel content of the two XLPE insulation materials increased firstly and then decreased with the increase of the thermal temperature and corresponding aging time, which shows that the cross-linking degree of the two XLPE increases first and then decreases. With the increase of the aging temperature and the aging time, the carbonyl index significantly increased for aged ordinary XLPE materials. However, the carbonyl index of the anti-water tree XLPE insulating materials changed smaller than that of the ordinary ones. Therefore, the anti-water tree XLPE insulating materials have better ability to inhibit thermal aging.

Mechanical Behavior of Aged EPDM Insulation of High-Voltage Cable Joints in Thermal-Oxidative Environment

Investigation on Thermal Aging and Degradation of XLPE for High Voltage Cable Applications

Effect of Tensile Stress on Insulation Properties of 500 Kv EHVAC XLPE Cable under Multi-Field Ageing

Effect of Thermal Aging on Breakdown Strength of Epdm Rubber

Breakdown Characteristics and Electrical Life Evaluation of 500 Kv EHVAC Cable Insulation at Different Temperatures

Effect of Thermal Ageing on Insulation Properties of 500 Kv DC XLPE Submarine Cable Insulation

Effect of Thermal Ageing on Physico-Chemical and Electrical Properties of EHVDC XLPE Cable Insulation

Influence of Thermal Aging on Dielectric Properties of High Voltage Cable Insulation Layer

Thermal aging characteristics and mechanism of insulation layer and semi-conductive shielding layer of high voltage cable

Effects of Thermal Aging on the Crystal Structures of the XLPE Cable Insulating Material at Different Temperatures

Research on Thermal Aging Characteristics and Mechanism of the Silicon Rubber Insulation Layer of Cable Joints

Influence of Oxygen Diffusion on Thermal Ageing of Cross-Linked Polyethylene Cable Insulation

Assessment of Thermally Aged XLPE Insulation Material under Extreme Operating Temperatures

Effect of Thermal Aging on Mechanical and Physical Performances of Resisting Water Tree XLPE

Effect of thermo-oxidative aging on thermal elongation performance of XLPE insulation for high-voltage cables

Thermal Aging Properties of 500 kV AC and DC XLPE Cable Insulation Materials

Influence of Thermal Ageing on the Optical Performance of XLPE Cable Insulation

Conductivity Properties of XLPE Insulation Used for HVDC Cable after Accelerated Thermal Ageing

Mechanism Characterization and Nondestructive Inspection Method of Thermal Degradation Faults in EPDM Cable Termination

Thermal aging property and breakdown property of submarine cable materials