Abstract:In this paper, we report on electrical and mechanical properties of isotactic polypropylene (PP) blended with polyolefin elastomer (POE) and propylene-based elastomer (PBE). Carrier trap distribution of the samples was estimated by isothermal surface potential decay measurement, while dc breakdown strength was measured through a pair of semicircle electrodes. Elongation at break and tensile strength were obtained to examine the variation in mechanical property of PP caused by the addition of elastomers. Furthermore, scanning electron microscope (SEM), differential scanning calorimetry (DSC), and dynamic mechanical analysis (DMA) have been employed to assist the understanding of morphology of the blends, thermal properties, and mechanical properties. Obtained results have indicated that with the increase of the elastomer content from 0 to 30 wt%, the trap depth appeared to be shallower and the dc breakdown strength tended to be reduced for both PP/PBE and PP/POE samples. Compared with PP/POE blend, PP/PBE blend had deeper trap depth, which should be responsible for its higher dc breakdown strength. In addition, PP/PBE blend has presented a better performance in elongation at break and tensile strength measurement. With the growth of the elastomer content, the crystallinity of the blends appeared to decrease, whereas the melting and the crystallization temperatures did not change remarkably. The SEM inspections and DMA results revealed better compatibility between PP and PBE compared with that between PP and POE, which should be the reason for the better electrical and mechanical properties of PP/PBE blend. The blend of PBE with low content could result in remarkably improved flexibility of PP with acceptable electrical strength for dc cable insulation.

Thermal Cycling Induced Aging on Polypropylene/Elastomer Blends for DC Cable Insulation

Investigation on Thermal Aging and Degradation of XLPE for High Voltage Cable Applications

Study on thermal cycling ageing resistance of performances of polypropylene/elastomer/boron nitride nanocomposites for high voltage direct current cable insulation

Influence of Thermal Aging on Insulation Properties of Voltage Stabilizer Blended Cross-Linked Polyethylene

Mechanical properties and space charge behavior of thermally aged polypropylene/elastomer blends

The Effect of DC Electro-thermal Ageing on Electrical Treeing in Polyethylene

An Investigation on the Evolution of Insulation Performance of BOPP Films for Power Capacitors under Multi Physical Fields Aging

Effect of Tensile Stress on Insulation Properties of 500 Kv EHVAC XLPE Cable under Multi-Field Ageing

Effect of Thermal Ageing on Insulation Properties of 500 Kv DC XLPE Submarine Cable Insulation

Thermal Properties and Space Charge Behavior of Thermally Aged Polypropylene/elastomer Blends Nanocomposite

Electrical Insulation Performance of Cross‐linked Polyethylene/mgo Nanocomposite Material for ±320 Kv High‐voltage Direct‐current Cables

Trap Distribution and Dielectric Breakdown of Isotactic Polypropylene/Propylene Based Elastomer With Improved Flexibility for DC Cable Insulation

Aging Behavior of Polypropylene As Cable Insulation under Gamma-Ray Irradiation

Research on the Thermal Aging Characteristics of Crosslinked Polyethylene Cables Based on Polarization and Depolarization Current Measurement

Mechanism Characterization and Nondestructive Inspection Method of Thermal Degradation Faults in EPDM Cable Termination

Study on high-temperature and high-voltage insulation characteristics of polypropylene blend with highly packed elastomeric domains for power cable applications

Characterization of Polypropylene Modified by Blending Elastomer and Nano-Silica

Thermal Aging State Evaluation of 10kV Polypropylene Cable

Thermal Aging Properties of 500 kV AC and DC XLPE Cable Insulation Materials

Enhanced Morphology-Dependent Tensile Property and Breakdown Strength of Impact Polypropylene Copolymer for Cable Insulation

The influence and mechanism of elastomer types on electrical and mechanical properties of polypropylene insulation materials for high voltage cables