Abstract:In this study, carbon blocks were fabricated using isotropic coke and coal tar pitch as raw materials, with a variation in pressure during cold isostatic pressing (CIP). The CIP pressure was set to 50, 100, 150, and 200 MPa, and the effect of the CIP pressure on the mechanical and electrical properties of the resulting carbon blocks was analyzed. Microstructural observations confirmed that, after the kneading, the surface of isotropic coke was covered with the pitch components. Subsequently, after the CIP, granules, which were larger than isotropic coke and the kneaded particles, were observed. The formation of these granules was attributed to the coalescence of kneaded particles under the applied pressing pressure. This granule formation was accompanied by the development of pores, some remaining within the granules, while others were extruded, thereby existing externally. The increase in the applied pressing pressure facilitated the formation of granules, and this microstructural development contributed to enhanced mechanical and electrical properties. At a pressing pressure of 100 MPa, the maximum flexural strength was achieved at 33.3 MPa, and the minimum electrical resistivity was reached at 60.1 μΩm. The higher the pressing pressure, the larger the size of the granules. Pores around the granules tended to connect and grow larger, forming crack-like structures. This microstructural change led to degraded mechanical and electrical properties. The isotropic ratio of the carbon blocks obtained in this study was estimated based on the coefficient of thermal expansion (CTE). The results confirmed that all carbon blocks obtained proved to be isotropic. In this study, a specimen type named CIP-100 exhibited the best performance in every aspect as an isotropic carbon block.

Carbon Blocks from Natural Flake Graphite and Mesophase Pitch: Fabrication Processing, Microstructre, Mechanical Property, and Electrical Perfromance

Graphite Blocks with Preferred Orientation and High Thermal Conductivity

Response surface optimization of pitch phase change densification using composite phenolic resin co-carbonization to prepare high performance carbon refractories

Effect of kneading and carbonization temperature on the structure of the carbon block for thermally conductive bulk graphites

The Effect of Oxygen Content in Binderless Cokes for High-Density Carbon Blocks from Coal Tar Pitch

Ultra-superior mechanical properties of multilayer graphene nanosheets reinforced carbon-graphite materials

Effect of Microstructural Change under Pressure during Isostatic Pressing on Mechanical and Electrical Properties of Isotropic Carbon Blocks

Response surface optimization and finite element simulation to prepare microporous carbon refractories via cold isostatic pressing

Changes in Physical Properties with Varying Impregnation Temperatures and Compression Times During Fabrication of Carbon Blocks Using Needle Cokes and Pitch

In-Situ Doping B4C Nanoparticles in Mesophase Pitch for Preparing Carbon Fibers with High Thermal Conductivity by Boron Catalytic Graphitization

Study on Preparation of Isotropic Graphite With Natural Amorphous Graphite

Composition Design of Block Copolymers for Porous Carbon Fibers

A Printed, Recyclable, Ultra-Strong, and Ultra-Tough Graphite Structural Material

Microstructure and properties of graphite nanoflakes/Cu matrix composites fabricated by pressureless sintering and subsequent thermo-mechanical treatment

Microstructure graphitization evolution and multi-scale, multi-mechanism synergistic enhancement of ultra-high strength carbon-graphite materials

Wettability of Natural Microcrystalline Graphite Filler with Pitch in Isotropic Graphite Preparation

Microstructure, electrical conductivity and mechanical properties of graphitization carbon foam derived from epoxy resin modified with coal tar pitch

Preparation and thermal conduction property of expanded graphite matrix composites

Microstructure and mechanical properties of carbon graphite composites reinforced by carbon nanofibers

Mesoscopic structure and properties of liquid crystalline mesophase pitch and its transformation into carbon fiber

Effects of Carbonization Pressure on Microstructure of Graphitized Pitch-derived Carbons