Abstract:Internal friction in two kinds of iron-manganese alloy which contain Mn 17.5% and Mn 12.8% respectively and one kind of copper-aluminum alloy containing 13% Al were measured with a torsion pendulum, and internal friction peaks were observed in the temperature range in which the martensite or reverse martensite transformation is taken place. The condition for the appearance of this internal friction peak is that it occurs only when accompanied by the process of martensite-type transformation.Systematic observations were made with iron-manganese alloy containing 17.5% Mn, and it was found that the height of internal friction peak increases with the increase of the rate of heating (or cooling) or the stress, decreases with the increase of the frequency of vibration or the carbon content in the specimen. All these may be explained by the reason that the more the amount of new phase has transformed in one period of vibration, the larger is the internal friction.The mechanism of the internal friction peak was discussed. The conclusion was reached that because of the suddeness of the formation of martensite, the applied external forces due to torsion pendulum may be considered as constant during the time of formation for martensite plates, and since half of the work done by the external forces during the alteration must be lost as confirmed by the calculation of interaction energies between stresses and iuhomogenities, it consequently gives rise to the substantial portion of internal friction. On the other hand, the stress-induced phase transformation also gives rise to a minor portion of internal friction.

INTERNAL FRICTION ASSOCIATED WITH MARTENSITIC AND PREMARTENSITIC PHASE TRANSFORMATION IN THE Khz AND THE MHz RANGE

A STUDY OF INTERNAL FRICTION ASSOCIATED WITH THE MARTENSITE TRANSFORMATION AT LOW FREQUENCY

Modulus Softening During the Γ→ɛ Martensitic Transformation in Fe–25Mn–6Si–5Cr–0.14N Alloys

Electron–transverse Acoustic Phonon Interaction in Martensitic Alloys

THE BEHAVIOR OF INTERNAL FRICTION ASSOCIATED WITH THE PROCESS OF MARTENSITE-TYPE TRANSFORMATION

Study of Stabilization of CuAlBe Alloy During Martensitic Transformation by Internal Friction

Low Frequency Damping Properties of Cu–Al–Be Alloy During the Phase Transformation

ULTRASONIC STUDY ON MARTENSITIC TRANSFORMATION IN AuCd ALLOY

In-situ Investigation Via High Energy X-ray Diffraction of Stress-Induced(0002)α→(110)β Transformation in a Ti-5.5Mo-7.2Al-4.5Zr-2.6Sn-2.1Cr Alloy

INTERNAL FRICTION AND ULTRASONIC ATTENUATION ASSOCIATED WITH THE NORMAL TO INCOMMENSURATE TRANSITION IN NiTi(Fe) ALLOY

Internal Friction Study on CuFe2O4∕PbZr0.53Ti0.47O3 Composites

INTERNAL FRICTION STUDY ON RELAXOR FERROELECTRIC MATERIALS

Studies on pre-bainitic transformation in CuZnAlMn alloy

INTERNAL FRICTION MEASUREMENT OF LOW- TEMPERATURE PHASE TRANSITIONS IN PZT CERAMICS

In situ high-energy X-ray diffraction study of thermally-activated martensitic transformation far below room temperature in CuZr-based bulk metallic glass composites

Internal Friction of the Phase Transition of Ge2Sb2Te5 Thin Film

Studies on Dynamics of Interfaces in Cu-Ai-Zn-Ni Alloy

A micro-mechanical model of non-thermo-elastic martensitic transformation

INTERNAL FRICTION AND DIELECTRIC PROPERTIES OF CuFe2O4-Pb(Mg1/3Nb2/3)O3 COMPOSITES

Thermoelastic Intermartensitic Transformation and Its Internal Stress Dependency Inni52mn24

Internal Friction and Young's Modulus of Titanium-Doped Lead Magnesium Niobate