Abstract:AISI 317 L stainless steel replaces 316 L grade in some applications due to its superior mechanical strength and corrosion resistance. Aiming at expanding its applicability to structural applications, ongoing studies are dedicated to overcoming the trade-off between strength and ductility. The stacking fault energy decreases with deformation temperature and favors stacking faulting, (nano)twinning and strain-induced martensite (SIM) formation, resulting in severe microstructural fragmentation. The effect of temperature on deformation behavior of AISI 317 L steel was investigated in samples rolled at room temperature to thickness reductions of 50% and 85% and at 77 K to reductions in thickness of 10% and 50%. The microstructural evolution was followed by scanning electron microscopy, Vickers microhardness, X-ray diffraction, magnetization, electron backscatter diffraction (EBSD) and electron channeling contrast imaging (ECCI). The nucleation sites in the early stages of the transformation sequence γ → ε → α' were identified in the 10% cryorolled sample. The highest volume fraction of α'-martensite reached 45.8% in the cryorolled steel to 50% rolling reduction. Much lower fractions were obtained for samples rolled to 10% reduction at 77 K (2%) and at room temperature to 50% (0.3%) and 85% reductions (1.6%). The texture components after cryorolling were Goss and Brass for austenite; rotated cube, α- and γ-fibers for δ-ferrite and α'-martensite. The ε-martensite presents the typical texture of hcp metals with a c/a ratio above the ideal value and 〈0001〉 − oriented tilted about 21° from the normal direction towards the rolling direction. The results show cryorolling as an effective method for enhancing SIM formation and promoting severe microstructural refinement in AISI 317 L stainless steel.

Influences of Volume Fraction, Shape of Martensite Islands on Mechanical Properties of 1cr17ni1 Stainless Steel

Microstructural Evolution and Mechanical Properties of 6cr13 Martensitic Stainless Steel Subjected to Cold Rolling and Heat Treatments

Influence of deformation-induced martensite on stress corrosion cracking of AISI 321 stainless steel

INFLUENCES OF VOLUME FRACTION,SHAPE AND STRENGTH OF MARTENSITE ISLANDS ON MECHANICAL PROPERTIES OF GRANULAR STRUCTURE STEELS

Influence of Material Inhomogeneity on the Mechanical Response of a Tempered Martensite Steel

Influence of the martensitic transformation on the deformation behaviour of an AISI 316 stainless steel at low temperatures

High Temperature Deformation Behavior and Constitutive Modelling for 05cr17ni4cu4nb Stainless Steel

Effects of Tempering Temperature on the Microstructure Evolution and Mechanical Properties of 16%cr–5%ni Super Martensitic Stainless Steel

Mechanical Behavior and Fatigue Performance of Austenitic Stainless Steel under Consideration of Martensitic Phase Transformation

Influence of Austenitizing Temperature on the Microstructure and Mechanical Properties of an Fe-Cr-Ni-Mo-Ti Maraging Stainless Steel

Strain-induced martensite formation in cryorolled AISI 317 L stainless steel

Effect of Martensitic Morphology on Mechanical Properties of an As-Quenched and Tempered 25crmo48v Steel

Influence of Grain Boundary Carbides on Mechanical Properties of High Nitrogen Austenitic Stainless Steel

Quantitative analysis of strength and plasticity of a 304 stainless steel based on the stress-strain curve

Effect of austenitic state before ferrite transformation on the mechanical behavior at an elevated temperature for seismic-resistant and fire-resistant constructional steel

Influence of Heat Treatment Temperature on Microstructure and Property of 00cr13ni5mo2 Supermartensitic Stainless Steel

Damage and Cracking Prediction of AISI 410 Martensitic Stainless Steel at Elevated Temperatures

Influence of temperature on tensile properties of T91 ferritic/martensitic steel

Investigation on Dynamic Recrystallization Behavior of Martensitic Stainless Steel

Exploring the effects of austenitizing conditions on the heterogeneous microstructure and mechanical properties of 11Cr–11Ni–Ti–Mo maraging stainless steel: Breakthrough in the strength-ductility trade-off

Mechanical Properties of Martensite Stainless Steel at High Temperature