Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Solvothermal Method Preparation of Nano Y2O2S:Eu 3+ and Research of Luminescence Property

Solvothermal route to synthesize well-dispersed YBO3:Eu nanocrystals.

Synthesis Of Nanocrystalline Y2o2s : Eu3+,Ti Long-Lasting Phosphorescen Material By Coprecipitation

Hydrothermal Method Synthesis and Characterization of Yvo4:Eu3+@Ypo4 Core-Shell Phosphor

Two-steps Prepared Monodisperse Li-doped Y2O3:Eu3+ Microspheres and Their Luminescence Properties

RESEARCH OF Y2O3∶Eu3+/Yb3+@SiO2 SOLAR ENERGY UPCONVERSION MATERIAL PREPARED BY SOL-GEL METHOD

Synthesis of Yttrium Oxide Nanocrystal Via Solvothermal Process

Preparation and photoluminescence of yttrium hydroxide and yttrium oxide doped with europium nanowires

Site-Selective Spectra and Time-Resolved Spectra of Nanocrystalline Y2o3 : Eu

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Synthesis and luminescence properties of Y 2O 3:Eu with flower-like microstructure

Luminescent Properties of Li+ Doped Nanosized Y2O3:Eu

Local Structure and Luminescence of Nanocrystalline Y2O3:Eu

Preparation And Characterization Of Nano-Yb2o3/Tio2 Particles

Facile synthesis of Y<sub>4</sub>O(OH)<sub>9</sub>NO<sub>3</sub>:Eu3+/Y<sub>2</sub>O<sub>3</sub>:Eu3+nanotubes and nanobundles from nanolamellar precursors

Synthesis and Enhanced Luminescence of Uniform and Well-Dispersed Quasispherical Yvo4:Ln(3+) (ln = Eu, Dy) Nanoparticles by A Solvothermal Method

Preparation and Luminescence of ZrO_2 Nanopowders Via Solvothermal Method

Preparation and Luminescent Properties of 1d Lu2o2s:Eu3+ Nanorods

Growth and Characterization of Single-Crystal Y2O3:Eu Nanobelts Prepared with a Simple Technique

General and Facile Method To Prepare Uniform Y<sub>2</sub>O<sub>3</sub>:Eu Hollow Microspheres