Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Preparation and Luminescent Properties of 1d Lu2o2s:Eu3+ Nanorods

Facile surfactant- and template-free synthesis and luminescent properties of one-dimensional lu 2O 3:Eu 3+ phosphors

Preparation and Luminescence Properties of Novel 3d Lu2o2s:Eu3+ Microstructures

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Controlled Synthesis and Luminescent Properties of Cubic Lu2O3:Eu3+ Nanocrystals

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

Hydrothermal Synthesis And Photoluminescence Of Eu2-Xsmxsn2o7 (X=0-2.0) Nanophosphors

Facile Synthesis And Luminescence Of Sr-5(Po4)(3)Ci:Eu2+ Nanorod Bundles Via A Hydrothermal Route

Shape controllable synthesis and luminescence properties of LuVO4:Ln3+ (Ln3+ = Eu, Sm, and Dy) nano/microstructure

Synthesis and Luminescent Properties of Monodisperse Core–shell Structured SiO2@Lu2O3:Eu3+ Microspheres

Controllable Synthesis and Luminescence Properties of One-Dimensional La2O3 and La2O3:Ln3+ (ln = Er, Eu, Tb) Nanorods with Different Aspect Ratios

Luminescent Properties in Relation to Controllable Phase and Morphology of Lubo3:Eu3+ Nano/Microcrystals Synthesized by Hydrothermal Approach

Hydrothermal synthesis and photoluminescence of single-crystalline LaVO4:Eu3+ nanorods/nanosheaves

Synthesis process and the luminescence properties of rare earth doped NaLa(WO4)2 nanoparticles

Local Structure of Nanocrystalline Lu2O3:Eu Studied by X-ray Absorption Spectroscopy

Luminescent Properties of Li+ Doped Nanosized Y2O3:Eu

Facile chemical conversion synthesis and luminescence properties of uniform Ln3+ (Ln = Eu, Tb)-doped NaLuF4 nanowires and LuBO3 microdisks.

Rare earth activated nanosized oxide phosphors: synthesis and optical properties

Synthesis and characterization of highly uniform Lu2O 3:Ln3+ (Ln = Eu, Er, Yb) luminescent hollow microspheres

Eu3+, Li+ Doped CaWO4 Nanorods: Synthesis, Emission-Decay Curves and Effective-Refractive Index

Multicolor Luminescence Properties of Ln(7)O(6)F(9): Re3+ (ln = Y, Lu; Re = Pr, Sm and Eu) Nano-Rods with Bifurcation