Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Controllable Synthesis and Luminescence Properties of One-Dimensional La2O3 and La2O3:Ln3+ (ln = Er, Eu, Tb) Nanorods with Different Aspect Ratios

Controllable Chemical Reaction Synthesis of Tb(OH)3 Nanorods and Their Photoluminescence Property

Controlled synthesis of light rare-earth hydroxide nanorods via a simple solution route

Controllable Synthesis and Luminescence Properties of La(OH)3 and La(OH)3:Tb3+ Nanocrystals with Multiform Morphologies

Generalized Synthesis of NaLn(MoO4)2 Nano/microcrystals (ln = La–Lu and Y): the Effects of Lanthanide Contraction, Structure, and Down-/Up-conversion Luminescence

Reductive Hydrothermal Synthesis of La(OH) 3 :Tb 3+ Nanorods As a New Green Emitting Phosphor

Electrodeposition of high aspect ratio LaPO 4 and LaPO 4 :Ln 3+ (Ln 3 + =Ce 3+ , Tb 3+ ) nanostructures

Controllable Synthesis and Tunable Luminescence of NaLa(MoO4)2 Hierarchical Architectures with Diverse Dimensions and Morphologies

Synthesis of Ultrafine Lanthanum Hydroxide Nanorods by A Simple Hydrothermal Process

Well-Defined Sodium Lanthanum Molybdate Microrods: Citrate-Assisted Hydrothermal Synthesis and Luminescence Properties

Homogeneous One-Dimensional Structured Tb(OH)3:Eu3+ Nanorods: Hydrothermal Synthesis, Energy Transfer, and Tunable Luminescence Properties

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

Amine-Assisted Synthesis and Characterization of Lanthanide Hydroxide Nanorods and Derived Oxides

Facile chemical conversion synthesis and luminescence properties of uniform Ln3+ (Ln = Eu, Tb)-doped NaLuF4 nanowires and LuBO3 microdisks.

Shape controllable synthesis and luminescence properties of LuVO4:Ln3+ (Ln3+ = Eu, Sm, and Dy) nano/microstructure

Preparation and Luminescent Properties of 1d Lu2o2s:Eu3+ Nanorods

Enhanced Luminescence Properties of Monodisperse Trioctylphosphine Oxide-Capped Nd3+-doped LaF3 Nanorods Without OH Groups

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Hydrothermal synthesis and photoluminescence of single-crystalline LaVO4:Eu3+ nanorods/nanosheaves

Synthesis and Luminescence Properties of Lanthanide Activator Ions Doped Strontium Molybdate Microspheres

General and Facile Synthesis, Formation Process, and Luminescence Properties of Well-Defined Rare Earth Oxides Hollow Spheres