Abstract:A duplex TiC and γ′-Ni3(Al,Ti) reinforced nickel composite was fabricated through hot-press sintering a 30 vol% Ti2AlC–Ni mixtures followed by thermal treatment method. Detailed microstructural detection was performed by adopting the route of high-resolution transmission electron microscopy. In situ generated submicron TiC particulate and nanosized L12-γ′ were homogeneously distributed in a fcc γ-Ni matrix. The high temperature tensile and compression behaviors of the TiC-γ′/Ni composites were evaluated in the temperature range of 25–800 °C. The results indicated that ultimate tensile and compression properties exhibited the dependence of temperatures. The tensile properties of the composite determined at 600 °C was 945 MPa, decreasing by 28.1% and 23.0% for elongation, compared to those of measured at room temperature (UTS = 1305 MPa, elongation = 5.35%). However, the yield strength exhibited the temperature independent until to 600 °C. The yield strength of the TiC-γ′/Ni composite are comparable with conventional superalloy under 600 °C, proving that TiC and γ′ particles constitute efficient reinforcements for Ni matrix according to thermal expansion dislocations strengthening, load-transfer and coherent strengthening mechanisms. The monotonic temperature dependence of yield strength at 600–800 °C indicates that plastic deformation of TiC-γ′/Ni composite follows the thermally activated mechanism. The TiC-γ′/Ni composite exhibited superior mechanical properties both at room and high temperatures, which can be ascribed to the synergistic strengthening effect in term of dislocation density, Orowan, coherent and atomic ordering strengthening mechanisms. The present work reveals the deformation behaviors of in situ TiC-γ′/Ni composite from room to high temperatures, which is critical to predict the failure and thereby optimize the microstructure to further enhance the high temperature properties of TiC-γ′/Ni composite.

High Temperature Deformation Mechanisms in WC-Ni 3al Cermets

Study on High Temperature Deformation Behavior of WC-10 Wt %ni3al Cemented Carbide

High Temperature Compressive Properties and Microstructure of WC-Ni3Al Cermets Prepared by Spark Plasma Sintering

A Molecular Dynamics Study on Mechanical Performance and Deformation Mechanisms in Nanotwinned NiCo-based Alloys with Nano-Precipitates under High Temperatures

Investigation on High Temperature Mechanical Behaviors of TiC-γ′ Reinforced Ni Composite

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

Preparation and Mechanical Properties of WC-10 Ni3Al Cemented Carbides with Plate-Like Triangular Prismatic WC Grains

Effect of Microstructure, Strain Rate, and Elevated Temperature on the Compression Property of Fe–Co–Ni–Cr–Zr Alloy

Mechanical Properties, Microstructure and Fracture Mechanism of 95W-3.5Ni-1.5fe Alloys at High Temperature

Effect of Ni on Mechanical Behavior of Al2O3/(W,Ti)C Ceramic Tool Materials at Ambient and Elevated Temperatures

High Temperature Deformation of Zrc Particulate-Reinforced Nb-Mo-W Composites

High temperature fracture mechanism of ultrafine WC-Co cemented carbides containing (Ti,W)C

Deformation mechanism of WC-12Co alloy under thermomechanical alternation

Deformation mechanisms of Al0.1CoCrFeNi at elevated temperatures

Correlation Between Microstructure and Deformation Mechanism in Ti66Nb13Cu8Ni6.8Al6.2 Composites at Ambient and Elevated Temperatures

Crystal Defects Responsible for Mechanical Behaviors of a WC-Co Composite at Room and High Temperatures - a Simulation Study.

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

Effect of temperature on high temperature plasticity of 95W-5(Ni/Fe/Co) alloy

High temperature deformation of ZrB2–SiC–AlN ceramic composite

Reaction Synthesis of Ni/Ni3Al Multilayer Composites Using Ni and Al Foils: High-temperature Tensile Properties and Deformation Behaviour

Effect of WC content on microstructure and mechanical properties of Ni3Al-bonded cermets