Abstract:For the purpose of elevated temperature service and weight reduction in aerospace vehicle applications, a novel Ti–Zr–Fe–Cu–Ni–Co–Mo filler metal was employed to join TiAl to Ni-based superalloy (GH536). The effects of brazing temperature on interfacial microstructure and chemical composition of the joints were analyzed. The representative joint microstructure from TiAl substrate to GH536 substrate was primarily composed of four characteristic layers in order: B2; Al3NiTi2; AlNi2Ti containing Cr-rich (Cr, Ni, Fe)ss (subscript ss represents solid solution), Ni-rich (Ni, Cr, Fe)ss and TiNi3; Cr-rich (Cr, Ni, Fe)ss containing AlNi2Ti, Ni-rich (Ni, Cr, Fe)ss and TiNi3. Layer IV has the majority of the brazing seam, while Layer II was the thinnest. And the thickness of Layer II was not affected by brazing temperature. With the increase in brazing temperature in the range of 1110–1170 °C, both the shear strength and the thickness of brazing seam firstly increased and then decreased. The joint performance was jointly controlled by the thickness of brazing seam, the amounts of microcracks and intermetallic compounds formed in brazing seam. The maximum shear strength of 183 MPa at room temperature was obtained together with a peak thickness when the joint was brazed at 1150 °C for 10 min and the shear fracture mainly occurred in the thinnest Layer II Al3NiTi2.<h3 class="a-plus-plus">Graphic abstract</h3>

Brazing Al<sub>2</sub>O<sub>3</sub> to Kovar Alloy with Ni/Ti/Ni Interlayer and Dramatic Increasing of Joint Strength after Thermal Cycles

Enhanced bonding of Al2O3/Al2O3 joints brazed by Ni50Ti50 master alloy interlayer

Effect of Cu interlayer with different thickness on microstructure and properties of Al2O3/Kovar joints brazed with Cu–Ti/Cu/BNi-2 composite filler

Interfacial microstructure and mechanical properties of ZTA/ZTA joints brazed with Ni-Ti filler metal

Brazing Between High Purity Alumina Ceramic and Oxygen-Free Copper

Brazing between high purity alumina ceramics and titanium

Secondary Phase Interaction at Interfaces of High-Strength Brazed Joints made using Liquid Phase Sintered Alumina Ceramics and Ag-Cu-Ti Braze Alloys

Brazing Al2O3 to 4J42 Using Ag–Cu–Ti/Cu/BNi-2 Composite Fillers with Different Thicknesses of Cu Interlayer

Microstructural characterization and mechanical properties of ZTA/ZTA joint brazed by Ni50Ti50 filler metal

Enhanced Mechanical Properties and Thermal Cycling Stability of Al2O3-4J42 Joints Brazed Using Ag–Cu–Ti/Cu/Ag–Cu Composite Filler

Microstructural Evolution and Mechanical Properties of Ti2AlNb/GH99 Superalloy Brazed Joints Using TiZrCuNi Amorphous Filler Alloy

Microstructure and shear property of high-temperature brazing of TiAl alloy and 316L stainless steel with a Ni-based amorphous filler

Brazing of C/C Composite and TiAl Alloy Using TiNiSi Filler Metal Added Cu Interlayer

Active Brazing of High Purity Alumina to Niobium Metal

A high-strength vacuum brazed TC4/316L joint with a Ti–Zr-based amorphous ribbon as the filler metal

Microstructure and mechanical properties of TiAl/Ni-based superalloy joints vacuum brazed with Ti–Zr–Fe–Cu–Ni–Co–Mo filler metal

Brazing of Ti2AlNb based alloy with amorphous Ti-Cu-Zr-Ni filler

Effects of Brazing Temperature on Microstructure and High-Temperature Strength of Joints Using a Novel Fourth-Generation Nickel-Based Single Crystal Superalloy

Understanding the oxidation behavior of TiAl alloy joints brazed using Ti and Ni based filler

Microstructure evolution and mechanical properties of TiAl/GH536 joints vacuum brazed with Ti–Zr–Cu–Ni filler metal

Microstructure and mechanical properties of Al2O3 ceramic and copper joints brazed with AgCuInTi brazing alloy

Brazing Al&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;3&lt;/sub&gt; to Kovar Alloy with Ni/Ti/Ni Interlayer and Dramatic Increasing of Joint Strength after Thermal Cycles